Specific Gravity
|
|
|
|
|
--
|
|
|
ASTM D792 |
|
--
|
|
lb/in³
|
ISO 1183 2 |
|
Melt Mass-Flow Rate (MFR) (220°C/10.0 kg)
|
|
g/10 min
|
ASTM D1238 |
|
Melt volume-flow rate (220°C/10.0 kg)
|
|
in³/10min
|
ISO 1133 2 |
|
Molding Shrinkage - Flow (0.126 in)
|
|
in/in
|
ASTM D955 |
|
Water Absorption (Saturation)
|
|
%
|
ISO 62 2 |
|
Tensile Modulus
|
|
|
|
|
0.126 in 3
|
|
psi
|
ASTM D638 |
|
--
|
|
psi
|
ISO 527-2 2 |
|
Tensile Strength
|
|
|
|
|
Yield, 0.126 in 4
|
|
psi
|
ASTM D638 |
|
Yield
|
|
psi
|
ISO 527-2 2 |
|
Tensile Elongation
|
|
|
|
|
Yield, 0.126 in 4
|
|
%
|
ASTM D638 |
|
Yield
|
|
%
|
ISO 527-2 2 |
|
Break, 0.126 in 4
|
|
%
|
ASTM D638 |
|
Nominal strain at break
|
|
%
|
ISO 527-2 2 |
|
Flexural Modulus 5 (0.126 in)
|
|
psi
|
ASTM D790 |
|
Flexural Strength 5 (0.126 in)
|
|
psi
|
ASTM D790 |
|
Charpy notched impact strength
|
|
|
ISO 179/1eA 2 |
|
-22°F
|
|
ft·lb/in²
|
|
|
73°F
|
|
ft·lb/in²
|
|
|
Charpy impact strength
|
|
|
ISO 179/1eU 2 |
|
-22°F
|
|
ft·lb/in²
|
|
|
73°F
|
|
|
|
|
Notched Izod Impact
|
|
|
ASTM D256 |
|
-22°F, 0.126 in
|
|
ft·lb/in
|
|
|
-22°F, 0.252 in
|
|
ft·lb/in
|
|
|
73°F, 0.126 in
|
|
ft·lb/in
|
|
|
73°F, 0.252 in
|
|
ft·lb/in
|
|
|
Rockwell Hardness (R-Scale)
|
|
|
ASTM D785 |
|
Deflection Temperature Under Load
|
|
|
ASTM D648 |
|
66 psi, Unannealed, 0.252 in
|
|
°F
|
|
|
264 psi, Unannealed, 0.252 in
|
|
°F
|
|
|
Glass Transition Temperature 6
|
|
°F
|
ISO 11357-2 2 |
|
Vicat Softening Temperature
|
|
|
|
|
--
|
|
°F
|
ASTM D1525 7 |
|
50°C/h, B (50N)
|
|
°F
|
ISO 306 2 |
|
CLTE
|
|
|
ISO 11359-2 2 |
|
Flow
|
|
in/in/°F
|
|
|
Transverse
|
|
in/in/°F
|
|
|
Volume Resistivity
|
|
ohm·cm
|
ASTM D257 |
|
Dielectric Strength
|
|
V/mil
|
ASTM D149 |
|
Relative Permittivity (1 MHz)
|
|
|
IEC 60250 2 |
|
Dissipation Factor (1 MHz)
|
|
|
IEC 60250 2 |
|
Arc Resistance (PLC)
|
|
|
ASTM D495 |
|
Flame Rating - UL
|
|
|
UL 94 |
|
0.0591 in
|
|
|
|
|
0.0630 in
|
|
|
|
|
0.118 in
|
|
|
|
|
0.126 in
|
|
|
|
|
0.236 in
|
|
|
|
|
Burning Behav. at thickness h (0.126 in, UL)
|
|
|
ISO 1210 2 |
|
RTI Str (0.0591 in)
|
|
°F
|
UL 746 |
|
RTI Imp (0.0591 in)
|
|
°F
|
UL 746 |
|
RTI Elec (0.0591 in)
|
|
°F
|
UL 746 |
|
Comparative Tracking Index (CTI) (PLC)
|
|
|
UL 746 |
|
High Voltage Arc Tracking Rate (HVTR) (PLC)
|
|
|
UL 746 |
|
Hot-wire Ignition (HWI) (PLC)
|
|
|
UL 746 |
|
0.0591 in
|
|
|
|
|
0.118 in
|
|
|
|
|
0.236 in
|
|
|
|
|
High Amp Arc Ignition (HAI) (PLC)
|
|
|
UL 746 |
|
0.0591 in
|
|
|
|
|
0.118 in
|
|
|
|
|
0.236 in
|
|
|
|
|