Density
|
|
--
|
g/cm³
|
ISO 1183/A |
|
Molding Shrinkage
|
|
|
|
ASTM D955 |
|
Flow
|
|
--
|
in/in
|
|
|
Across Flow
|
|
--
|
in/in
|
|
|
Water Absorption (24 hr)
|
|
--
|
%
|
ASTM D570 |
|
Tensile Modulus
|
|
|
|
|
|
--
|
|
|
psi
|
ASTM D638 |
|
73°F
|
|
--
|
psi
|
ISO 527-2 |
|
212°F
|
|
--
|
psi
|
ISO 527-2 |
|
Tensile Stress
|
|
|
|
|
|
Break, 73°F
|
|
--
|
psi
|
ISO 527-2 |
|
Break, 212°F
|
|
--
|
psi
|
ISO 527-2 |
|
--
|
|
|
psi
|
ASTM D638 |
|
Tensile Elongation
|
|
|
|
|
|
Break
|
|
|
%
|
ASTM D638 |
|
Break, 73°F
|
|
--
|
%
|
ISO 527-2 |
|
Break, 212°F
|
|
--
|
%
|
ISO 527-2 |
|
Flexural Modulus
|
|
|
|
|
|
--
|
|
|
psi
|
ASTM D790 |
|
73°F
|
|
--
|
psi
|
ISO 178 |
|
212°F
|
|
--
|
psi
|
ISO 178 |
|
Flexural Strength
|
|
|
|
|
|
--
|
|
|
psi
|
ASTM D790 |
|
212°F
|
|
--
|
psi
|
ISO 178 |
|
73°F
|
|
--
|
psi
|
ISO 178 |
|
Compressive Strength
|
|
--
|
psi
|
ASTM D695 |
|
Shear Strength
|
|
|
psi
|
ASTM D732 |
|
Charpy Notched Impact Strength (73°F)
|
|
--
|
ft·lb/in²
|
ISO 179/1eA |
|
Charpy Unnotched Impact Strength (73°F)
|
|
--
|
ft·lb/in²
|
ISO 179/1eU |
|
Notched Izod Impact
|
|
|
|
|
|
--
|
|
|
ft·lb/in
|
ASTM D256 |
|
73°F
|
|
--
|
ft·lb/in²
|
ISO 180/1A |
|
Unnotched Izod Impact
|
|
|
|
|
|
--
|
|
--
|
ft·lb/in
|
ASTM D256 |
|
73°F
|
|
--
|
ft·lb/in²
|
ISO 180/1U |
|
Heat Deflection Temperature
|
|
|
|
|
|
66 psi, Unannealed
|
|
--
|
°F
|
ISO 75-2/B |
|
264 psi, Unannealed
|
|
--
|
°F
|
ISO 75-2/A |
|
264 psi, Annealed
|
|
--
|
°F
|
ASTM D648 |
|
Melting Temperature
|
|
--
|
°F
|
ISO 11357-3, ASTM D3418 |
|
CLTE
|
|
|
|
ASTM E831 |
|
Flow: 32 to 212°F
|
|
--
|
in/in/°F
|
|
|
Flow: 212 to 392°F
|
|
--
|
in/in/°F
|
|
|
Transverse: 32 to 212°F
|
|
--
|
in/in/°F
|
|
|
Transverse: 212 to 392°F
|
|
--
|
in/in/°F
|
|
|
|
Product names can be difficult to match. You may have searched any one of these terms to find this product: Amodel® AT-6115 HS, Amodel AT6115 HS, Amodel® , Amodel, AmodelAT6115HS, AT, AT-6115 HS, AT6115 HS, AT:6115 HS, AT/6115 HS, AT+6115 HS, AT_6115 HS, AT 6115 HS, AT6115, 6115HS, AT6115HS, AT_6115HS, Polyphthalamide, PPA, Polyamide, Nylon, Solvay Specialty, 6115AT
|
|
|
Features may also be described by the following terms: Fast Cycle, Rapid Cycle, Productivity, Fast Molding Cycle, High Flow, High Melt, High MFI, High Elongation, Heat Stabilized, Heat-ageing Stabilized, Heat Ageing Stabilized, Heat-aging Stabilized, Heat Aging Stabilized, Good Mold Release, Easy Release, Good Demolding.
|
|
|
Uses may also be described by the following terms: Machine Parts, Mechanical Parts, Machine/Mechanical Parts, Housings, Housing, Industrial Parts, Automotive Applications, Automotive Sector, Valves, Valve Parts.
|
|
|
This plastic material has approval for 9 automotive specifications from the following agencies (the number in parentheses shows the number of specifications for that agency): FORD (2), DELPHI (2), GM (1), ISO (1), ASTM (3).
|
|
|
Product names can be difficult to match. You may have searched any one of these terms to find this product: Amodel® AT-6115 HS, Amodel AT6115 HS, Amodel® , Amodel, AmodelAT6115HS, AT, AT-6115 HS, AT6115 HS, AT:6115 HS, AT/6115 HS, AT+6115 HS, AT_6115 HS, AT 6115 HS, AT6115, 6115HS, AT6115HS, AT_6115HS, Polyphthalamide, PPA, Polyamide, Nylon, Solvay Specialty, 6115AT
|