POLYFORT® FIPP 30 T K1005 A. Schulman Eur Polypropylene Copolymer (Talc Filler, 30%)

Product Description

30% talc filled PP-Copolymer; long term heat stabilized

General

Material Status

Availability

Filler / Reinforcement

Processing Method

Physical	Nominal Value	Unit	Test Method
Density		g/cm³	ISO 1183/A
Melt Volume-Flow Rate (MVR) (230°C/2.16 kg)		in³/10min	ISO 1133
Mechanical	Nominal Value	Unit	Test Method
Tensile Modulus		psi	ISO 527-2/1A/1
Tensile Stress (Yield)		psi	ISO 527-2/1A/50
Tensile Strain (Yield)		%	ISO 527-2/1A/50
Flexural Modulus		psi	ISO 178
Flexural Strength		psi	ISO 178
Flexural Strain at Flexural Strength		%	ISO 178
Impact	Nominal Value	Unit	Test Method
Charpy Notched Impact Strength			ISO 179/1eA
-22°F		ft·lb/in²
73°F		ft·lb/in²
Charpy Unnotched Impact Strength			ISO 179/1eU
-22°F		ft·lb/in²
73°F		ft·lb/in²
Hardness	Nominal Value	Unit	Test Method
Ball Indentation Hardness (H 358/30)		psi	ISO 2039-1
Thermal	Nominal Value	Unit	Test Method
Heat Deflection Temperature
66 psi, Unannealed		°F	ISO 75-2/Bf
264 psi, Unannealed		°F	ISO 75-2/Af
Vicat Softening Temperature
--		°F	ISO 306/A50
--		°F	ISO 306/B50
Electrical	Nominal Value	Unit	Test Method
Surface Resistivity		ohm	IEC 60093
Volume Resistivity		ohm·cm	IEC 60093
Flammability	Nominal Value	Unit	Test Method
Burning Rate		in/min	ISO 3795
Flammability Classification			IEC 60695-11-10, -20
0.0591 in
0.118 in
Related Terminology
Product names can be difficult to match. You may have searched any one of these terms to find this product: POLYFORT® FIPP 30 T K1005, POLYFORT FIPP 30 T K1005, POLYFORT® , POLYFORT, POLYFORTFIPP30TK1005, FIPP 30 T K 1005, FIPP 30 T K1005, FIPP30, 30T, TK, K1005, FIPP30TK1005, Polypropylene Copolymer, PP Copolymer, Polypropylene, PP, A. Schulman Eur, PolypropyleneCopolymer, PPCopolymer, 30FIPP

Notes

¹Typical properties: these are not to be construed as specifications.

POLYFORT® FIPP 30 T K1005