| Specific Gravity |
|
|
|
|
--
|
|
|
ASTM D792 |
|
--
|
|
g/cm³
|
ISO 1183 |
| Melt Mass-Flow Rate (MFR) |
|
|
|
|
190°C/1.05 kg
|
|
g/10 min
|
ASTM D1238 |
|
190°C/2.16 kg
|
|
g/10 min
|
ISO 1133 |
| Melt Volume-Flow Rate (MVR) (190°C/2.16 kg) |
|
in³/10min
|
ISO 1133 |
| Molding Shrinkage |
|
|
|
|
Flow: 24 hr, 0.126 in
|
|
in/in
|
ASTM D955 |
|
Across Flow: 24 hr, 0.126 in
|
|
in/in
|
ASTM D955 |
|
Across Flow: 0.0787 in
|
|
%
|
ISO 294-4 |
|
Flow: 0.0787 in
|
|
%
|
ISO 294-4 |
| Water Absorption |
|
|
|
|
73°F, 24 hr
|
|
%
|
ASTM D570 |
|
Saturation, 73°F
|
|
%
|
ASTM D570, ISO 62 |
|
Equilibrium, 73°F, 50% RH
|
|
%
|
ASTM D570 |
|
Equilibrium, 73°F, 50% RH
|
|
%
|
ISO 62 |
| Tensile Modulus |
|
|
|
|
73°F 3
|
|
psi
|
ASTM D638 |
|
73°F
|
|
psi
|
ISO 527-2 |
| Tensile Strength |
|
|
|
|
Yield, 73°F 3
|
|
psi
|
ASTM D638 |
|
Yield, 73°F
|
|
psi
|
ISO 527-2 |
|
158°F 3
|
|
psi
|
ASTM D638 |
|
212°F 3
|
|
psi
|
ASTM D638 |
| Tensile Elongation |
|
|
|
|
Yield, 73°F 3
|
|
%
|
ASTM D638 |
|
Yield, 73°F
|
|
%
|
ISO 527-2 |
|
Break, 73°F 3
|
|
%
|
ASTM D638 |
|
Break, 158°F 3
|
|
%
|
ASTM D638 |
|
Break, 212°F 3
|
|
%
|
ASTM D638 |
|
Break, 73°F
|
|
%
|
ISO 527-2 |
| Nominal Tensile Strain at Break (73°F) |
|
%
|
ISO 527-2 |
| Tensile Creep Modulus |
|
|
ISO 899-1 |
|
1 hr
|
|
psi
|
|
|
1000 hr
|
|
psi
|
|
| Flexural Modulus |
|
|
|
|
73°F
|
|
psi
|
ASTM D790 |
|
158°F
|
|
psi
|
ASTM D790 |
|
212°F
|
|
psi
|
ASTM D790 |
|
73°F
|
|
psi
|
ISO 178 |
| Flexural Strength |
|
|
|
|
5.0% Strain, 73°F
|
|
psi
|
ASTM D790 |
|
3.5% Strain, 73°F
|
|
psi
|
ISO 178 |
| Shear Strength (73°F) |
|
psi
|
ASTM D732 |
| Charpy Notched Impact Strength |
|
|
ISO 179/1eA |
|
-22°F
|
|
ft·lb/in²
|
|
|
73°F
|
|
ft·lb/in²
|
|
| Charpy Unnotched Impact Strength |
|
|
ISO 179/1eU |
|
-22°F
|
|
|
|
|
73°F
|
|
|
|
| Notched Izod Impact |
|
|
|
|
-40°F
|
|
ft·lb/in
|
ASTM D256 |
|
73°F
|
|
ft·lb/in
|
ASTM D256 |
|
-40°F
|
|
ft·lb/in²
|
ISO 180/1A |
|
73°F
|
|
ft·lb/in²
|
ISO 180/1A |
| Unnotched Izod Impact (73°F) |
|
|
ASTM D4812 |
| Tensile Impact Strength 4 (73°F) |
|
ft·lb/in²
|
ASTM D1822 |
| Rockwell Hardness |
|
|
|
|
M-Scale
|
|
|
ASTM D785 |
|
R-Scale
|
|
|
ASTM D785, ISO 2039-2 |
|
M-Scale
|
|
|
ISO 2039-2 |
| Deflection Temperature Under Load |
|
|
|
|
66 psi, Unannealed
|
|
°F
|
ASTM D648 |
|
66 psi, Unannealed
|
|
°F
|
ISO 75-2/B |
|
264 psi, Unannealed
|
|
°F
|
ASTM D648 |
|
264 psi, Unannealed
|
|
°F
|
ISO 75-2/A |
|
264 psi, Annealed
|
|
°F
|
ISO 75-2/A |
| Melting Temperature 5 |
|
°F
|
ISO 11357-3, ASTM D3418 |
| CLTE |
|
|
|
|
Flow: -40 to 73°F
|
|
in/in/°F
|
ASTM E831, ISO 11359-2 |
|
Flow: 73 to 131°F
|
|
in/in/°F
|
ASTM E831, ISO 11359-2 |
|
Flow: 131 to 212°F
|
|
in/in/°F
|
ASTM E831 |
|
Flow: -40 to 86°F
|
|
in/in/°F
|
ISO 11359-2 |
|
Flow: 131 to 212°F
|
|
in/in/°F
|
ISO 11359-2 |
|
Transverse: -40 to 73°F
|
|
in/in/°F
|
ASTM E831, ISO 11359-2 |
|
Transverse: 73 to 131°F
|
|
in/in/°F
|
ASTM E831, ISO 11359-2 |
|
Transverse: 131 to 212°F
|
|
in/in/°F
|
ASTM E831 |
|
Transverse: 131 to 212°F
|
|
in/in/°F
|
ISO 11359-2 |
| Surface Resistivity |
|
|
|
|
--
|
|
ohms
|
ASTM D257 |
|
--
|
|
ohms
|
IEC 60093 |
| Volume Resistivity |
|
|
|
|
73°F
|
|
ohm·cm
|
ASTM D257 |
|
--
|
|
ohm·cm
|
IEC 60093 |
| Dielectric Strength 6 (73°F, 0.126 in) |
|
V/mil
|
ASTM D149 |
| Dielectric Constant |
|
|
|
|
73°F, 1 MHz
|
|
|
ASTM D150 |
|
73°F, 100 Hz
|
|
|
IEC 60250 |
|
73°F, 1 MHz
|
|
|
IEC 60250 |
| Dissipation Factor (73°F, 1 MHz) |
|
|
ASTM D150, IEC 60250 |
| Comparative Tracking Index |
|
V
|
IEC 60112 |
| Flame Rating - UL |
|
|
UL 94 |
|
0.0295 in
|
|
|
|
|
0.0591 in
|
|
|
|
|
0.118 in
|
|
|
|
|
0.236 in
|
|
|
|
| Flammability Classification |
|
|
IEC 60695-11-10, -20 |
|
0.0295 in
|
|
|
|
|
0.0591 in
|
|
|
|
|
0.118 in
|
|
|
|
|
0.236 in
|
|
|
|
| Oxygen Index |
|
%
|
ISO 4589-2 |
| RTI Str |
|
|
UL 746 |
|
0.0295 in
|
|
°F
|
|
|
0.0591 in
|
|
°F
|
|
|
0.118 in
|
|
°F
|
|
|
0.236 in
|
|
°F
|
|
| RTI Imp |
|
|
UL 746 |
|
0.0295 in
|
|
°F
|
|
|
0.0591 in
|
|
°F
|
|
|
0.118 in
|
|
°F
|
|
|
0.236 in
|
|
°F
|
|
| RTI Elec |
|
|
UL 746 |
|
0.0295 in
|
|
°F
|
|
|
0.0591 in
|
|
°F
|
|
|
0.118 in
|
|
°F
|
|
|
0.236 in
|
|
°F
|
|
| Comparative Tracking Index (CTI) (0.118 in) |
|
V
|
UL 746 |
|
This supplier and product may also be known by these terms: Derlin
Product names can be difficult to match. You may have searched any one of these terms to find this product: Delrin® 100 NC010, Delrin 100 NC010, Delrin® , Delrin, Delrin100NC010, 100 NC 010, 100 NC010, 100NC, NC010, 100NC010, Acetal Homopolymer, Acetal Homopolymer, Acetal (POM) Homopolymer, Acetal POM Homopolymer, Acetal, pom, DuPont, AcetalPOMHomopolymer, NC100
|
|
Features may also be described by the following terms: High Viscosity, Good Toughness, Tough, High Strength, High Stiffness, High Molecular Weight, High MW, Good Dimensional Stability, Dimensionally Stable, Good Creep Resistance, Creep Resistant, High Impact Resistance, Ultrasonic Weldable.
|
|
Uses may also be described by the following terms: Housings, Housing, Engineering Parts, Tubing, Tube.
|
|
This plastic material has approval for 4 automotive specifications from the following agencies (the number in parentheses shows the number of specifications for that agency): FORD (1), ASTM (1), CHRYSLER (1), GM (1).
|