Density
|
|
g/cm³
|
ISO 1183 |
|
Melt Mass-Flow Rate (MFR) (190°C/2.16 kg)
|
|
g/10 min
|
ISO 1133 |
|
Tensile Modulus
|
|
psi
|
ISO 527-2 |
|
Tensile Stress (Yield)
|
|
psi
|
ISO 527-2 |
|
Coefficient of Friction (Blown Film)
|
|
|
ISO 8295 |
|
Film Thickness - Tested
|
|
mil
|
|
|
Film Thickness - Recommended / Available
|
|
|
|
|
Tensile Strength
|
|
|
ISO 527-3 |
|
MD: 2.0 mil, Blown Film
|
|
psi
|
|
|
TD: 2.0 mil, Blown Film
|
|
psi
|
|
|
Tensile Elongation
|
|
|
ISO 527-3 |
|
MD: Break, 2.0 mil, Blown Film
|
|
%
|
|
|
TD: Break, 2.0 mil, Blown Film
|
|
%
|
|
|
Dart Drop Impact (2.0 mil, Blown Film)
|
|
g
|
ASTM D1709 |
|
Vicat Softening Temperature
|
|
°F
|
ISO 306/A50 |
|
Melting Temperature (DSC)
|
|
°F
|
ISO 3146 |
|
Gloss
|
|
|
ASTM D2457 |
|
20°, 1.97 mil, Blown Film
|
|
|
|
|
60°, 1.97 mil, Blown Film
|
|
|
|
|
Haze (1.97 mil, Blown Film)
|
|
%
|
ASTM D1003 |
|
Failure Energy (2.8 mil)
|
|
ft·lb/in
|
DIN 53373 |
|
Film properties tested using 50 µm thickness blown film extruded at a melt temperature of 180°C and a blow-up ratio of 1:2.5.
|
|
This supplier and product may also be known by these terms: LyondellBasell Industries, Lyondell, Basell, Bassell, Basell Polyolefins, Bassel
Product names can be difficult to match. You may have searched any one of these terms to find this product: Lupolen 2420 D, Lupolen , Lupolen2420D, 2420 D, 2420D, Polyethylene, Low Density, Polyethylene Low Density, LDPE, Polyethylene, PE, LyondellBasell, PolyethyleneLowDensity, D2420
|
|
Features may also be described by the following terms: Good Toughness, Tough, Good Tear Strength, Good Processability, Easy Processing.
|
|
Uses may also be described by the following terms: Shrink Wrap.
|