Melt Mass-Flow Rate (MFR) (200°C/5.0 kg)
|
|
g/10 min
|
ISO 1133 |
|
Molding Shrinkage
|
|
%
|
ISO 294-4 |
|
Tensile Modulus (73°F)
|
|
psi
|
ISO 527-2/1A/1 |
|
Tensile Stress
|
|
|
ISO 527-2/1A/50 |
|
Yield, 73°F
|
|
psi
|
|
|
Break, 73°F
|
|
psi
|
|
|
Tensile Strain (Break, 73°F)
|
|
%
|
ISO 527-2/1A/50 |
|
Flexural Strength 2 (73°F, 0.157 in)
|
|
psi
|
ISO 178 |
|
Charpy Notched Impact Strength (73°F)
|
|
ft·lb/in²
|
ISO 179/1eA |
|
Charpy Unnotched Impact Strength
|
|
|
|
|
73°F
|
|
ft·lb/in²
|
ISO 179/1eU |
|
73°F
|
|
|
ISO 179/1fU |
|
Notched Izod Impact Strength (73°F)
|
|
ft·lb/in²
|
ISO 180/1A |
|
Unnotched Izod Impact Strength (73°F)
|
|
ft·lb/in²
|
ISO 180/1U |
|
Ball Indentation Hardness (H 358/30, 0.157 in)
|
|
psi
|
ISO 2039-1 |
|
Heat Deflection Temperature (264 psi, Unannealed)
|
|
°F
|
ISO 75-2/Af |
|
Vicat Softening Temperature
|
|
|
|
|
--
|
|
°F
|
ISO 306/A50 |
|
--
|
|
°F
|
ISO 306/A120 |
|
--
|
|
°F
|
ISO 306/B50 |
|
--
|
|
°F
|
ISO 306/B120 |
|
Surface Resistivity
|
|
ohms
|
IEC 60093 |
|
Volume Resistivity
|
|
ohm·cm
|
IEC 60093 |
|
Relative Permittivity (50 Hz)
|
|
|
IEC 60250 |
|
Dissipation Factor (50 Hz)
|
|
|
IEC 60250 |
|
Comparative Tracking Index (0.118 in, Solution A)
|
|
V
|
IEC 60112 |
|
Electric Strength (0.157 in, in Oil)
|
|
V/mil
|
IEC 60243-1 |
|
Flame Rating - UL (0.0630 in)
|
|
|
UL 94 |
|
Glow Wire Ignition Temperature (0.118 in)
|
|
°F
|
IEC 60695-2-13 |
|
Arc Resistance, IEC 61 621, 3 mm: 108 sec
|
|
Product names can be difficult to match. You may have searched any one of these terms to find this product: KRASTEN 562 E, KRASTEN , KRASTEN562E, 562 E, 562E, PS, Polystyrene, High Impact, Polystyrene High Impact, PS (HIPS), PS HIPS, Polystyrene, Kaucuk, PolystyreneHighImpact, PSHIPS, E562
|
|
Features may also be described by the following terms: High Impact Resistance.
|