Specific Gravity
|
|
|
|
|
--
|
|
|
ASTM D792 |
|
--
|
|
g/cm³
|
ISO 1183 |
|
Melt Mass-Flow Rate (MFR) (250°C/2.16 kg)
|
|
g/10 min
|
ASTM D1238, ISO 1133 |
|
Molding Shrinkage
|
|
|
ASTM D955 |
|
Flow
|
|
in/in
|
|
|
Across Flow
|
|
in/in
|
|
|
Water Absorption
|
|
|
|
|
73°F, 24 hr
|
|
%
|
ASTM D570, ISO 62 |
|
Saturation
|
|
%
|
ASTM D570 |
|
Saturation, 73°F
|
|
%
|
ISO 62 |
|
Granule Humidity
|
|
%
|
Internal Method |
|
Tensile Modulus
|
|
psi
|
ASTM D638, ISO 527-2 |
|
Tensile Strength (Break)
|
|
psi
|
ASTM D638, ISO 527-2 |
|
Tensile Elongation (Break)
|
|
%
|
ASTM D638, ISO 527-2 |
|
Flexural Modulus
|
|
psi
|
ASTM D790, ISO 178 |
|
Flexural Strength
|
|
|
|
|
--
|
|
psi
|
ISO 178 |
|
Break
|
|
psi
|
ASTM D790 |
|
Charpy Notched Impact Strength 2 (73°F)
|
|
ft·lb/in²
|
ASTM D256, ISO 179 |
|
Notched Izod Impact (73°F, 0.126 in)
|
|
ft·lb/in
|
ISO 180, ASTM D256 |
|
Rockwell Hardness (R-Scale)
|
|
|
ASTM D785 |
|
Deflection Temperature Under Load (264 psi, Unannealed)
|
|
°F
|
ASTM D648, ISO 75-2/A |
|
Max. Continuous Use Temperature
|
|
|
IEC 60216 |
|
-- 3
|
|
°F
|
|
|
-- 4
|
|
°F
|
|
|
-- 5
|
|
°F
|
|
|
-- 6
|
|
°F
|
|
|
Vicat Softening Temperature
|
|
°F
|
ISO 306/B50, ASTM D1525 7 |
|
Ball Pressure Test (329°F)
|
|
|
VDE 0470 |
|
Melting Temperature
|
|
°F
|
ASTM D211, ISO 121 |
|
CLTE - Flow (-22 to 86°F)
|
|
in/in/°F
|
ASTM D696 |
|
Volume Resistivity
|
|
ohm·cm
|
ASTM D257 |
|
Comparative Tracking Index (Solution A)
|
|
V
|
IEC 60112 |
|
Flame Rating - UL (0.0630 in)
|
|
|
UL 94 |
|
Glow Wire Ignition Temperature (0.0787 in)
|
|
°F
|
IEC 60695-2-13 |
|
Oxygen Index
|
|
%
|
ASTM D2863 |
|
Product names can be difficult to match. You may have searched any one of these terms to find this product: TAROMID B 280 G10, TAROMID B , TAROMIDB280G10, TAROMIDB, B 280 G 10, B280 G10, B280, 280 G 10, B280G10, 280 G10, 280G, G10, 280G10, Polyamide 6, Nylon 6, Polyamide, Nylon, pa6, Taro Plast, Polyamide6, Nylon6, G280, 280B
|
|
Generic Name may also be described by the following terms: PA6.
|
|
Features may also be described by the following terms: Good Dimensional Stability, Dimensionally Stable, Low Shrinkage, Heat Stabilized, Heat-ageing Stabilized, Heat Ageing Stabilized, Heat-aging Stabilized, Heat Aging Stabilized, Good Mold Release, Easy Release, Good Demolding, Good UV Resistance, UV Resistant, Ultraviolet Resistant, Ultraviolet Light Resistant.
|