TAROMID B 280 G5 X0

Polyamide 6

Glass Fiber Reinforcement, 25%

Supplied by Taro Plast S.p.A.

The technical datasheet with complete property values for TAROMID B 280 G5 X0 is available to members of the Prospector Plastics Database.
Register to view full datasheet.
Register to View Full Datasheet
Product Description
Polyamide 6 glass fiber reinforced 25%, UL94 V0 self extinguishing, good flame proofing also at low thickness, good flow and good mechanical properties.

UL94 V0 approuved all colors at 0,97 mm. UL746B approved.

Available: different colors, heat stabilized (H), release agent (W), and without PBDE/PBDF.
General  
Material Status 
  • Commercial: Active
Availability 
  • Europe
Filler / Reinforcement 
  • Glass Fiber Reinforcement, 25% Filler by Weight
Additive 
  • Heat Stabilizer
  • Mold Release
  
Features 
  • Flame Retardant
  • Good Flow
  • Good Mold Release
  • Heat Stabilized
  • Self Extinguishing
Appearance 
  • Colors Available
Forms 
  • Pellets
Processing Method 
  • Injection Molding
Physical
Nominal Value
Unit
Test Method
Specific Gravity
      
--
 
 ASTM D792
--
g/cm³
 ISO 1183
Molding Shrinkage
     ASTM D955
Flow
in/in
  
Across Flow
in/in
  
Water Absorption
      
73°F, 24 hr
%
 ASTM D570, ISO 62
Saturation
%
 ASTM D570
Saturation, 73°F
%
 ISO 62
Granule Humidity
%
 Internal Method
Mechanical
Nominal Value
Unit
Test Method
Tensile Modulus
psi
 ASTM D638, ISO 527-2
Tensile Strength (Break)
psi
 ASTM D638, ISO 527-2
Tensile Elongation (Break)
%
 ASTM D638, ISO 527-2
Flexural Modulus
psi
 ASTM D790, ISO 178
Flexural Strength
      
--
psi
 ISO 178
Break
psi
 ASTM D790
Impact
Nominal Value
Unit
Test Method
Charpy Notched Impact Strength 2 (73°F)
ft·lb/in²
 ASTM D256, ISO 179
Notched Izod Impact (73°F, 0.126 in)
ft·lb/in
 ISO 180, ASTM D256
Hardness
Nominal Value
Unit
Test Method
Rockwell Hardness (R-Scale)
 
 ASTM D785
Thermal
Nominal Value
Unit
Test Method
Deflection Temperature Under Load (264 psi, Unannealed)
°F
 ASTM D648, ISO 75-2/A
Max. Continuous Use Temperature
     IEC 60216
-- 3
°F
  
-- 4
°F
  
-- 5
°F
  
-- 6
°F
  
Vicat Softening Temperature
      
--
°F
 ASTM D1525 7, ISO 306/A50 7
--
°F
 ASTM D1525 8, ISO 306/B50 8
Ball Pressure Test (329°F)
 
 VDE 0470
Melting Temperature
°F
 ASTM D211, ISO 121
CLTE - Flow (-22 to 86°F)
in/in/°F
 ASTM D696
Electrical
Nominal Value
Unit
Test Method
Volume Resistivity
ohm·cm
 ASTM D257
Comparative Tracking Index (Solution A)
V
 IEC 60112
Flammability
Nominal Value
Unit
Test Method
Flame Rating - UL (0.0382 in)
 
 UL 94
Glow Wire Ignition Temperature (0.0787 in)
°F
 IEC 60695-2-13
Oxygen Index
%
 ASTM D2863
Related Terminology
Product names can be difficult to match. You may have searched any one of these terms to find this product: TAROMID B 280 G5 X0, TAROMID B , TAROMIDB280G5X0, TAROMIDB, B 280 G 5 X 0, B280 G5 X0, B280, 280 G 5 X 0, B280G5X0, 280 G5 X0, 280G, G5, 5X, X0, 280G5X0, Polyamide 6, Nylon 6, Polyamide, Nylon, pa6, Taro Plast, Polyamide6, Nylon6, G280, 280B
Generic Name
Generic Name may also be described by the following terms: PA6.
Features
Features may also be described by the following terms: Self Extinguishing, Self-Extinguishing, Good Flow, Heat Stabilized, Heat-ageing Stabilized, Heat Ageing Stabilized, Heat-aging Stabilized, Heat Aging Stabilized, Good Mold Release, Easy Release, Good Demolding.
Injection
Nominal Value
Unit
 
Drying Temperature
      
--
°F
  
Pre-heater
°F
  
Drying Time
      
--
hr
  
Pre-heater
hr
  
Processing (Melt) Temp
°F
  
Mold Temperature
°F
  
Injection Rate
 
  
Notes
1Typical properties: these are not to be construed as specifications.
26x4x50 mm
320000 hrs
4Heat Stabilized, 20000 hrs
5Short Term
6Heat Stabilized, Short Term
7Rate A (50°C/h), Loading 1 (10 N)
8Rate A (50°C/h), Loading 2 (50 N)
 
IDES
Copyright © 2012 IDES
The information presented on this datasheet was acquired by IDES from the producer of the material. IDES makes substantial efforts to assure the accuracy of this data. However, IDES assumes no responsibility for the data values and strongly encourages that upon final material selection, data points are validated with the material supplier.