Specific Gravity
|
|
|
|
|
--
|
|
|
ASTM D792 |
|
--
|
|
g/cm³
|
ISO 1183 |
|
Melt Mass-Flow Rate (MFR) (250°C/2.16 kg)
|
|
g/10 min
|
ASTM D1238, ISO 1133 |
|
Molding Shrinkage
|
|
|
ASTM D955 |
|
Flow
|
|
in/in
|
|
|
Across Flow
|
|
in/in
|
|
|
Water Absorption
|
|
|
|
|
73°F, 24 hr
|
|
%
|
ASTM D570, ISO 62 |
|
Saturation
|
|
%
|
ASTM D570 |
|
Saturation, 73°F
|
|
%
|
ISO 62 |
|
Granule Humidity
|
|
%
|
Internal Method |
|
Tensile Modulus
|
|
psi
|
ASTM D638, ISO 527-2 |
|
Tensile Strength (Break)
|
|
psi
|
ASTM D638, ISO 527-2 |
|
Tensile Elongation (Break)
|
|
%
|
ASTM D638, ISO 527-2 |
|
Flexural Modulus
|
|
psi
|
ASTM D790, ISO 178 |
|
Flexural Strength
|
|
|
|
|
--
|
|
psi
|
ISO 178 |
|
Break
|
|
psi
|
ASTM D790 |
|
Charpy Notched Impact Strength 2 (73°F)
|
|
ft·lb/in²
|
ASTM D256, ISO 179 |
|
Notched Izod Impact
|
|
|
ISO 180, ASTM D256 |
|
-4°F, 0.126 in
|
|
ft·lb/in
|
|
|
73°F, 0.126 in
|
|
ft·lb/in
|
|
|
Rockwell Hardness (R-Scale)
|
|
|
ASTM D785 |
|
Deflection Temperature Under Load
|
|
|
|
|
66 psi, Unannealed
|
|
°F
|
ASTM D648, ISO 75-2/B |
|
264 psi, Unannealed
|
|
°F
|
ASTM D648, ISO 75-2/A |
|
Max. Continuous Use Temperature
|
|
|
IEC 60216 |
|
-- 3
|
|
°F
|
|
|
-- 4
|
|
°F
|
|
|
-- 5
|
|
°F
|
|
|
-- 6
|
|
°F
|
|
|
Vicat Softening Temperature
|
|
|
|
|
--
|
|
°F
|
ASTM D1525 7, ISO 306/A50 7 |
|
--
|
|
°F
|
ASTM D1525 8, ISO 306/B50 8 |
|
Ball Pressure Test (401°F)
|
|
|
VDE 0470 |
|
Melting Temperature
|
|
°F
|
ASTM D211, ISO 121 |
|
CLTE - Flow (-22 to 86°F)
|
|
in/in/°F
|
ASTM D696 |
|
Volume Resistivity
|
|
ohm·cm
|
ASTM D257 |
|
Dielectric Strength (0.0787 in)
|
|
V/mil
|
ASTM D149 |
|
Comparative Tracking Index
|
|
|
IEC 60112 |
|
Solution A
|
|
V
|
|
|
Solution B
|
|
V
|
|
|
Flame Rating - UL
|
|
|
UL 94 |
|
0.0382 in
|
|
|
|
|
0.0630 in
|
|
|
|
|
0.126 in
|
|
|
|
|
Glow Wire Ignition Temperature (0.0787 in)
|
|
°F
|
IEC 60695-2-13 |
|
Oxygen Index
|
|
%
|
ASTM D2863 |
|
Product names can be difficult to match. You may have searched any one of these terms to find this product: TAROLOX 10 G4, TAROLOX , TAROLOX10G4, 10 G 4, 10 G4, 10G, G4, 10G4, Polybutylene Terephthalate, PBT, Polyester, Taro Plast, PolybutyleneTerephthalate, G10
|
|
Features may also be described by the following terms: Good Flow, Good Surface Finish, Good Dimensional Stability, Dimensionally Stable, Heat Stabilized, Heat-ageing Stabilized, Heat Ageing Stabilized, Heat-aging Stabilized, Heat Aging Stabilized, Good Mold Release, Easy Release, Good Demolding.
|