TAROLOX 111 G6 DX0 Taro Plast Polyethylene Terephthalate (Glass Fiber Reinforcement, 30%)

Product Description

PET glass fiber reinforced 30%, self extinguishing V0 without PBDE/PBDF, good flame proofing also at low thickness, high temperature resistance, good flow, very good mechanical, thermal and electrical properties, low moisture absorption, good dimensional stability. Product must be dryed before moulding.

Available: different colors, release agent (W).

General

Material Status

Commercial: Active

Availability

Europe

Filler / Reinforcement

Glass Fiber Reinforcement, 30% Filler by Weight

Additive

Mold Release

Features

Flame Retardant

Good Dimensional Stability

Good Electrical Properties

Good Flow

Good Mold Release

High Heat Resistance

Low Moisture Absorption

Self Extinguishing

Appearance

Colors Available

Forms

Pellets

Processing Method

Injection Molding

Physical	Nominal Value	Unit	Test Method
Specific Gravity
--			ASTM D792
--		g/cm³	ISO 1183
Molding Shrinkage			ASTM D955
Flow		in/in
Across Flow		in/in
Water Absorption (73°F, 24 hr)		%	ASTM D570, ISO 62
Granule Humidity		%	Internal Method
Mechanical	Nominal Value	Unit	Test Method
Tensile Modulus		psi	ASTM D638, ISO 527-2
Tensile Strength (Break)		psi	ASTM D638, ISO 527-2
Tensile Elongation (Break)		%	ASTM D638, ISO 527-2
Flexural Modulus		psi	ASTM D790, ISO 178
Flexural Strength
--		psi	ISO 178
Break		psi	ASTM D790
Impact	Nominal Value	Unit	Test Method
Charpy Notched Impact Strength² (73°F)		ft·lb/in²	ASTM D256, ISO 179
Charpy Unnotched Impact Strength² (73°F)		ft·lb/in²	ASTM D256, ISO 179
Notched Izod Impact			ISO 180, ASTM D256
-4°F, 0.126 in		ft·lb/in
73°F, 0.126 in		ft·lb/in
Hardness	Nominal Value	Unit	Test Method
Rockwell Hardness (R-Scale)			ASTM D785
Thermal	Nominal Value	Unit	Test Method
Deflection Temperature Under Load
66 psi, Unannealed		°F	ASTM D648, ISO 75-2/B
264 psi, Unannealed		°F	ASTM D648, ISO 75-2/A
Max. Continuous Use Temperature
--³		°F	IEC 60216
--		°F	UL 746B
Vicat Softening Temperature		°F	ISO 306/B50, ASTM D1525⁴
Ball Pressure Test (473°F)			VDE 0470
Melting Temperature		°F	ASTM D211, ISO 121
CLTE - Flow (-22 to 86°F)		in/in/°F	ASTM D696
Electrical	Nominal Value	Unit	Test Method
Volume Resistivity		ohm·cm	ASTM D257
Dielectric Strength (0.0394 in)		V/mil	ASTM D149
Comparative Tracking Index (Solution A)		V	IEC 60112
Flammability	Nominal Value	Unit	Test Method
Flame Rating - UL			UL 94
0.0382 in
0.0630 in
0.126 in
Glow Wire Ignition Temperature (0.0787 in)		°F	IEC 60695-2-13
Oxygen Index		%	ASTM D2863
Related Terminology
Product names can be difficult to match. You may have searched any one of these terms to find this product: TAROLOX 111 G6 DX0, TAROLOX , TAROLOX111G6DX0, 111 G 6 DX 0, 111 G6 DX0, 111G, G6, 6DX, DX0, 111G6DX0, Polyethylene Terephthalate, PET, Polyester, Taro Plast, PolyethyleneTerephthalate, G111
Features
Features may also be described by the following terms: Self Extinguishing, Self-Extinguishing, High Heat Resistance, Good Flow, Low Moisture Absorption, Low Water Absorption, Water Resistant, Moisture Resistant, Good Dimensional Stability, Dimensionally Stable, Good Mold Release, Easy Release, Good Demolding, Good Electrical Properties.

Injection	Nominal Value	Unit
Drying Temperature
--		°F
Pre-heater		°F
Processing (Melt) Temp		°F
Mold Temperature		°F
Injection Rate

Notes

¹Typical properties: these are not to be construed as specifications.

²6x4x50 mm

³20000 hrs

⁴Rate A (50°C/h), Loading 2 (50 N)

TAROLOX 111 G6 DX0

Polyethylene Terephthalate

Glass Fiber Reinforcement, 30%

Supplied by Taro Plast S.p.A.