Specific Gravity
|
|
|
|
|
--
|
|
|
ASTM D792 |
|
--
|
|
g/cm³
|
ISO 1183 |
|
Melt Volume-Flow Rate (MVR) (250°C/5.0 kg)
|
|
in³/10min
|
ISO 1133 |
|
Molding Shrinkage
|
|
|
|
|
Flow: 0.126 in
|
|
in/in
|
Internal Method |
|
Across Flow: 0.126 in
|
|
in/in
|
Internal Method |
|
Across Flow 3
|
|
%
|
ISO 294-4 |
|
Flow 3
|
|
%
|
ISO 294-4 |
|
Across Flow: 0.0787 in
|
|
%
|
ISO 294-4 |
|
Flow: 0.0787 in
|
|
%
|
ISO 294-4 |
|
Water Absorption (Equilibrium, 73°F, 0.0394 in, 50% RH)
|
|
%
|
ISO 62 |
|
Tensile Modulus
|
|
|
|
|
73°F
|
|
psi
|
ASTM D638 |
|
73°F
|
|
psi
|
ISO 527-2 |
|
Tensile Stress
|
|
|
|
|
Break, 73°F
|
|
psi
|
ISO 527-2 |
|
73°F
|
|
psi
|
ASTM D638 |
|
Tensile Elongation (Break, 73°F)
|
|
%
|
ASTM D638, ISO 527-2 |
|
Flexural Modulus
|
|
|
|
|
73°F
|
|
psi
|
ASTM D790 |
|
73°F
|
|
psi
|
ISO 178 |
|
Flexural Strength (73°F)
|
|
psi
|
ASTM D790 |
|
Charpy Notched Impact Strength
|
|
|
ISO 179/1eA |
|
-22°F
|
|
ft·lb/in²
|
|
|
73°F
|
|
ft·lb/in²
|
|
|
Charpy Unnotched Impact Strength
|
|
|
ISO 179/1eU |
|
-22°F
|
|
ft·lb/in²
|
|
|
73°F
|
|
ft·lb/in²
|
|
|
Notched Izod Impact
|
|
|
|
|
73°F
|
|
ft·lb/in
|
ASTM D256 |
|
-40°F
|
|
ft·lb/in²
|
ISO 180/1A |
|
-22°F
|
|
ft·lb/in²
|
ISO 180/1A |
|
73°F
|
|
ft·lb/in²
|
ISO 180/1A |
|
Unnotched Izod Impact (73°F)
|
|
ft·lb/in
|
ASTM D4812 |
|
Deflection Temperature Under Load
|
|
|
|
|
66 psi, Unannealed
|
|
°F
|
ASTM D648 |
|
264 psi, Unannealed
|
|
°F
|
ASTM D648 |
|
264 psi, Unannealed
|
|
°F
|
ISO 75-2/A |
|
Glass Transition Temperature
|
|
°F
|
ISO 11357-2 |
|
Melting Temperature 4
|
|
°F
|
ISO 11357-3, ASTM D3418 |
|
CLTE
|
|
|
ISO 11359-2 |
|
Flow: 73 to 131°F
|
|
in/in/°F
|
|
|
Transverse: 73 to 131°F
|
|
in/in/°F
|
|
|
Surface Resistivity
|
|
ohms
|
ASTM D257 |
|
Volume Resistivity (73°F)
|
|
ohm·cm
|
ASTM D257 |
|
Dielectric Strength 5 (73°F, 0.126 in)
|
|
V/mil
|
ASTM D149 |
|
Dielectric Constant
|
|
|
ASTM D150 |
|
73°F, 1 kHz
|
|
|
|
|
73°F, 1 MHz
|
|
|
|
|
Dissipation Factor
|
|
|
ASTM D150 |
|
73°F, 1 kHz
|
|
|
|
|
73°F, 1 MHz
|
|
|
|
|
Flame Rating - UL
|
|
|
UL 94 |
|
0.0295 in
|
|
|
|
|
0.0591 in
|
|
|
|
|
0.118 in
|
|
|
|
|
Flammability Classification
|
|
|
IEC 60695-11-10, -20 |
|
0.0295 in
|
|
|
|
|
0.0591 in
|
|
|
|
|
0.118 in
|
|
|
|
|
RTI Str
|
|
|
UL 746 |
|
0.0295 in
|
|
°F
|
|
|
0.0591 in
|
|
°F
|
|
|
0.118 in
|
|
°F
|
|
|
RTI Imp
|
|
|
UL 746 |
|
0.0295 in
|
|
°F
|
|
|
0.0591 in
|
|
°F
|
|
|
0.118 in
|
|
°F
|
|
|
RTI Elec
|
|
|
UL 746 |
|
0.0295 in
|
|
°F
|
|
|
0.0591 in
|
|
°F
|
|
|
0.118 in
|
|
°F
|
|
|
Comparative Tracking Index (CTI)
|
|
V
|
UL 746 |
|
Product names can be difficult to match. You may have searched any one of these terms to find this product: Crastin® LW9320 NC010, Crastin LW9320 NC010, Crastin® , Crastin, CrastinLW9320NC010, LW 9320 NC 010, LW9320 NC010, LW9320, 9320NC, NC010, LW9320NC010, Polybutylene Terephthalate Alloy, PBT Alloy, Polyester, DuPont, PolybutyleneTerephthalateAlloy, PBTAlloy, 9320LW
|
|
Features may also be described by the following terms: Low Warpage, Low Warp, Warp Resistant, Warpage Resistant, Good Processability, Easy Processing, Good Dimensional Stability, Dimensionally Stable, Good Chemical Resistance, Chemical Resistant, Pleasing Surface Appearance, Low Moisture Absorption, Low Water Absorption, Water Resistant, Moisture Resistant, Ultrasonic Weldable.
|
|
Uses may also be described by the following terms: Housings, Housing, Automotive Applications, Automotive Sector.
|
|
This plastic material has approval for 1 automotive specifications from the following agencies (the number in parentheses shows the number of specifications for that agency): GM (1).
|