Specific Gravity
|
|
|
|
|
--
|
|
|
ASTM D792 |
|
--
|
|
g/cm³
|
ISO 1183 |
|
Melt Mass-Flow Rate (MFR)
|
|
|
|
|
230°C/2.16 kg
|
|
g/10 min
|
ASTM D1238 |
|
230°C/2.16 kg
|
|
g/10 min
|
ISO 1133 |
|
Melt Volume-Flow Rate (MVR) (230°C/2.16 kg)
|
|
in³/10min
|
ISO 1133 |
|
Molding Shrinkage
|
|
|
ISO 294-4 |
|
Across Flow: 0.0787 in
|
|
%
|
|
|
Flow: 0.0787 in
|
|
%
|
|
|
Water Absorption
|
|
|
|
|
73°F, 24 hr
|
|
%
|
ASTM D570, ISO 62 |
|
Saturation, 73°F
|
|
%
|
ISO 62 |
|
Equilibrium, 73°F, 50% RH
|
|
%
|
ISO 62 |
|
Tensile Strength
|
|
|
|
|
Break, 73°F
|
|
psi
|
ASTM D638 |
|
Break, 73°F
|
|
psi
|
ISO 527-2/1BA |
|
5.0% Strain, 73°F
|
|
psi
|
ASTM D638 |
|
15% Strain, 73°F
|
|
psi
|
ASTM D638 |
|
10% Strain, 73°F
|
|
psi
|
ASTM D638 |
|
50% Strain, 73°F
|
|
psi
|
ISO 527-2/1BA |
|
Tensile Stress
|
|
|
ISO 527-2/1BA |
|
10% Strain: 73°F
|
|
psi
|
|
|
5% Strain: 73°F
|
|
psi
|
|
|
Tensile Elongation
|
|
|
|
|
Break, 73°F
|
|
%
|
ASTM D638 |
|
Break, 73°F
|
|
%
|
ISO 527-2/1BA |
|
Nominal Tensile Strain at Break (73°F)
|
|
%
|
ISO 527-2/1BA |
|
Flexural Modulus
|
|
|
|
|
-40°F
|
|
psi
|
ASTM D790 |
|
73°F
|
|
psi
|
ASTM D790 |
|
257°F
|
|
psi
|
ASTM D790 |
|
73°F
|
|
psi
|
ISO 178 |
|
Charpy Notched Impact Strength
|
|
|
ISO 179/1eA |
|
-40°F
|
|
|
|
|
-22°F
|
|
|
|
|
73°F
|
|
|
|
|
Charpy Unnotched Impact Strength
|
|
|
ISO 179/1eU |
|
-22°F
|
|
|
|
|
73°F
|
|
|
|
|
Notched Izod Impact
|
|
|
|
|
-40°F
|
|
|
ASTM D256, ISO 180/1A |
|
73°F
|
|
|
ISO 180/1A |
|
Durometer Hardness
|
|
|
|
|
Shore D
|
|
|
ASTM D2240 |
|
Shore D
|
|
|
ISO 868 |
|
Shore D, 15 sec
|
|
|
ISO 868 |
|
Heat Deflection Temperature (66 psi, Unannealed)
|
|
°F
|
ISO 75-2/B |
|
Brittleness Temperature
|
|
|
|
|
--
|
|
°F
|
ASTM D746 |
|
--
|
|
°F
|
ISO 974 |
|
Glass Transition Temperature
|
|
°F
|
ISO 11357-2 |
|
Melting Temperature
|
|
|
|
|
-- 2
|
|
°F
|
ISO 11357-3 |
|
--
|
|
°F
|
ASTM D3418 |
|
CLTE
|
|
|
|
|
Flow: -40 to 73°F
|
|
in/in/°F
|
ASTM E831, ISO 11359-2 |
|
Flow: 73 to 131°F
|
|
in/in/°F
|
ASTM E831 |
|
Flow: 131 to 248°F
|
|
in/in/°F
|
ASTM E831, ISO 11359-2 |
|
Flow: 73 to 131°F
|
|
in/in/°F
|
ISO 11359-2 |
|
Transverse: -40 to 73°F
|
|
in/in/°F
|
ASTM E831, ISO 11359-2 |
|
Transverse: 73 to 131°F
|
|
in/in/°F
|
ASTM E831 |
|
Transverse: 131 to 248°F
|
|
in/in/°F
|
ASTM E831, ISO 11359-2 |
|
Transverse: 73 to 131°F
|
|
in/in/°F
|
ISO 11359-2 |
|
Surface Resistivity
|
|
ohm
|
IEC 60093 |
|
Volume Resistivity
|
|
ohm·cm
|
IEC 60093 |
|
Relative Permittivity
|
|
|
IEC 60250 |
|
73°F, 100 Hz
|
|
|
|
|
73°F, 1 MHz
|
|
|
|
|
Dissipation Factor
|
|
|
IEC 60250 |
|
73°F, 100 Hz
|
|
|
|
|
73°F, 1 MHz
|
|
|
|
|
Comparative Tracking Index
|
|
V
|
IEC 60112 |
|
Electric Strength (73°F)
|
|
V/mil
|
IEC 60243-1 |
|
Oxygen Index
|
|
%
|
ISO 4589-2 |
|
Drying Temperature - Blow Molding
|
|
°F
|
|
|
Drying Time - Dehumidified Dryer, Blow Molding
|
|
hr
|
|
|
Processing Moisture Content - Blow Molding
|
|
%
|
|
|
Product names can be difficult to match. You may have searched any one of these terms to find this product: Hytrel® HTR8139BK, Hytrel HTR8139BK, Hytrel® , Hytrel, HytrelHTR8139BK, HTR 8139 BK, HTR8139BK, HTR8139, 8139BK, Thermoplastic Copolyester Elastomer, TPC-ET, TPCET, TPC:ET, TPC/ET, TPC+ET, TPC_ET, TPC ET, Thermoplastic Elastomer, TPE, DuPont, ThermoplasticCopolyesterElastomer, ThermoplasticElastomer, 8139HTR
|
|
Features may also be described by the following terms: Heat Stabilized, Heat-ageing Stabilized, Heat Ageing Stabilized, Heat-aging Stabilized, Heat Aging Stabilized, High Viscosity, Good Melt Strength, Good Abrasion Resistance, Abrasion Resistant, Low Temperature Flexibility.
|
|
Uses may also be described by the following terms: Cast Film, Tubing, Tube, Wire and Cable Applications, Wire & Cable Applications, Automotive Applications, Automotive Sector.
|