Specific Gravity
|
|
|
|
|
--
|
|
|
ASTM D792 |
|
--
|
|
lb/in³
|
ISO 1183 2 |
|
Melt Mass-Flow Rate (MFR) (330°C/2.16 kg)
|
|
g/10 min
|
ASTM D1238, ISO 1133 |
|
Melt volume-flow rate (330°C/2.16 kg)
|
|
in³/10min
|
ISO 1133 2 |
|
Water Absorption
|
|
|
|
|
73°F, 24 hr
|
|
%
|
ASTM D570 |
|
Saturation, 73°F
|
|
%
|
ASTM D570 |
|
Saturation
|
|
%
|
ISO 62 2 |
|
Equilibrium
|
|
%
|
ISO 62 2 |
|
Tensile Modulus
|
|
|
|
|
73°F 3
|
|
psi
|
ASTM D638 |
|
--
|
|
psi
|
ISO 527-2 2 |
|
Tensile Strength
|
|
|
|
|
Yield, 73°F
|
|
psi
|
ASTM D638 |
|
Yield
|
|
psi
|
ISO 527-2 2 |
|
Tensile Elongation
|
|
|
|
|
Yield, 73°F
|
|
%
|
ASTM D638 |
|
Yield
|
|
%
|
ISO 527-2 2 |
|
Nominal strain at break
|
|
%
|
ISO 527-2 2 |
|
Flexural Modulus 4
|
|
psi
|
ISO 178 |
|
Flexural Strength 4
|
|
psi
|
ISO 178 |
|
Charpy notched impact strength
|
|
|
ISO 179/1eA 2 |
|
-22°F
|
|
ft·lb/in²
|
|
|
73°F
|
|
ft·lb/in²
|
|
|
Charpy impact strength
|
|
|
ISO 179/1eU 2 |
|
-22°F
|
|
|
|
|
73°F
|
|
|
|
|
Ball Indentation Hardness
|
|
psi
|
ISO 2039-1 |
|
Deflection Temperature Under Load
|
|
|
|
|
66 psi, Unannealed, 0.250 in
|
|
°F
|
ASTM D648 |
|
66 psi
|
|
°F
|
ISO 75-2 2 |
|
264 psi, Unannealed, 0.250 in
|
|
°F
|
ASTM D648 |
|
264 psi, Annealed
|
|
°F
|
ISO 75-2/A |
|
264 psi
|
|
°F
|
ISO 75-2 2 |
|
Vicat Softening Temperature
|
|
|
|
|
--
|
|
°F
|
ASTM D1525 5 |
|
--
|
|
°F
|
ISO 306/B120 |
|
50°C/h, B (50N)
|
|
°F
|
ISO 306 2 |
|
CLTE
|
|
|
ASTM D696 2, ISO 11359-2 2 |
|
Flow
|
|
in/in/°F
|
|
|
Transverse
|
|
in/in/°F
|
|
|
Surface Resistivity
|
|
|
|
|
--
|
|
ohm
|
ASTM D257 |
|
--
|
|
ohm
|
IEC 60093 2 |
|
Volume Resistivity
|
|
|
|
|
--
|
|
ohm·cm
|
ASTM D257 |
|
--
|
|
ohm·in
|
IEC 60093 2 |
|
Dielectric Strength
|
|
|
|
|
73°F, 0.125 in, in Oil 6
|
|
V/mil
|
ASTM D149 |
|
--
|
|
V/mil
|
IEC 60243-1 2 |
|
Dielectric Constant
|
|
|
|
|
73°F, 60 Hz
|
|
|
ASTM D150 |
|
73°F, 1 MHz
|
|
|
ASTM D150 |
|
100 Hz
|
|
|
IEC 60250 2 |
|
1 MHz
|
|
|
IEC 60250 2 |
|
Dissipation Factor
|
|
|
|
|
73°F, 60 Hz
|
|
|
ASTM D150 |
|
73°F, 1 MHz
|
|
|
ASTM D150 |
|
100 Hz
|
|
|
IEC 60250 2 |
|
1 MHz
|
|
|
IEC 60250 2 |
|
Comparative Tracking Index
|
|
|
|
|
Solution B
|
|
V
|
IEC 60112 |
|
--
|
|
|
IEC 60112 2 |
|
Flame Rating - UL
|
|
|
UL 94 |
|
0.0591 in
|
|
|
|
|
0.118 in
|
|
|
|
|
Burning Behav. at 1.6mm nom. thickn. (0.06 in, UL)
|
|
|
ISO 1210 2 |
|
Burning Behav. at thickness h (0.118 in, UL)
|
|
|
ISO 1210 2 |
|
Oxygen Index
|
|
%
|
ASTM D2863 2, ISO 4589-2 2 |
|
Refractive Index
|
|
|
|
|
--
|
|
|
ASTM D542 |
|
-- 7
|
|
|
ISO 489 |
|
Transmittance (125 mil)
|
|
%
|
ASTM D1003 |
|
Haze (125 mil)
|
|
%
|
ASTM D1003 |
|
Comparative tracking index CTI M, IEC 60112, Solution B: <100 M
Dielectric constant, Tinfoil electrodes, ASTM D150, 1 MHz: 2.9
Dielectric constant, Tinfoil electrodes, ASTM D150, 60 Hz: 2.9
Dielectric strength, ASTM D149, Short time under oil at 73 °F, 0.125 in: >400 V/mil
Dissipation factor, Tinfoil electrodes, ASTM D150, 60 Hz: 0.001
Dissipation factor, Tinfoil electrodes, ASTM D150, 1 MHz: 0.01
Electrolytic corrosion, IEC 60426: A1
Luminous transmittance (clear transparent materials), ISO 13468-2, 1 mm: 90 %
Specific volume, ASTM D792: 24.1 in³/lb
Surface resistivity, ASTM D257: >1.0E16 Ohm
Volume resistivity, Tinfoil electrodes, ASTM D257: >1.0E16 Ohm*m
|
|
Product names can be difficult to match. You may have searched any one of these terms to find this product: Apec® 1805, Apec 1805, Apec® , Apec, Apec1805, 1805, Polycarbonate, PC, Bayer
|
|
Features may also be described by the following terms: Good Mold Release, Easy Release, Good Demolding.
|
|
Uses may also be described by the following terms: Automotive Applications, Automotive Sector.
|
|
This plastic material has approval for 6 automotive specifications from the following agencies (the number in parentheses shows the number of specifications for that agency): FORD (1), CHRYSLER (3), GM (2).
|
|
This plastic material has 3 certifications from the following agencies (the number in parentheses shows the number of certifications for that agency): EU (3).
|