Radici Compounds N60G13L

Polyamide 6

Glass Fiber Reinforcement, 13%

Supplied by Radici Plastics USA, Inc.

The technical datasheet with complete property values for Radici Compounds N60G13L is available to members of the Prospector Plastics Database.
Register to view full datasheet.
Register to View Full Datasheet
Product Description
N60G13L is a nylon 6 compound, reinforced with 13% glass fiber, which significantly improves strength and rigidity especially at elevated temperatures, while maintaining good toughness. For molded parts, which are to be exposed to high temperatures for prolonged periods of time, the use of a heat stabilized compound is recommended.

N60G13HSL incorporates a conventional stabilizer system, which offers excellent protection against thermal aging, but will tint the natural color, normally to a greenish hue.

N60G13L offers the high flow, easy processing and outstanding surface gloss characteristic of nylon 6 resins, and is lubricated for improved feed and mold release.

Reinforced nylon 6 compounds offer a unique combination of strength and rigidity, excellent static and dynamic fatigue resistance, natural lubricity, and resistance to the effects of broad range of chemicals, oils and solvents, and are therefore used for a very wide range of applications in every end-use category.
General  
Material Status 
  • Commercial: Active
Availability 
  • North America
Filler / Reinforcement 
  • Glass Fiber Reinforcement, 13% Filler by Weight
Additive 
  • Lubricant
Features 
  • Fatigue Resistant
  • Good Chemical Resistance
  • Good Mold Release
  • Good Processability
  • Good Strength
  • Good Toughness
  • High Flow
  • High Gloss
  • Lubricated
  • Medium Rigidity
  • Oil Resistant
  • Solvent Resistant
Forms 
  • Pellets
Processing Method 
  • Injection Molding
Physical
Nominal Value
Unit
Test Method
Specific Gravity
 
 ASTM D792
Molding Shrinkage - Flow (0.125 in)
in/in
 ASTM D955
Water Absorption (24 hr)
%
 ASTM D570
Mechanical
Nominal Value
Unit
Test Method
Tensile Strength (Break, 73°F)
psi
 ASTM D638
Tensile Elongation (Break, 73°F)
%
 ASTM D638
Flexural Modulus (73°F)
psi
 ASTM D790
Flexural Strength (73°F)
psi
 ASTM D790
Impact
Nominal Value
Unit
Test Method
Notched Izod Impact (73°F, 0.125 in)
ft·lb/in
 ASTM D256
Hardness
Nominal Value
Unit
Test Method
Rockwell Hardness (R-Scale)
 
 ASTM D785
Thermal
Nominal Value
Unit
Test Method
Deflection Temperature Under Load (264 psi, Unannealed)
°F
 ASTM D648
Melting Temperature
°F
 ASTM D789
Related Terminology
Product names can be difficult to match. You may have searched any one of these terms to find this product: Radici Compounds N60G13L, Radici Compounds , RadiciCompoundsN60G13L, RadiciCompounds, CompoundsN 60 G 13 L, CompoundsN60G13L, CompoundsN60, Compounds, N 60 G 13 L, N60G13L, N60, 60G, G13, 13L, Polyamide 6, Nylon 6, Polyamide, Nylon, pa6, Radici USA, Polyamide6, Nylon6, 60N, 60CompoundsN
Generic Name
Generic Name may also be described by the following terms: PA6.
Features
Features may also be described by the following terms: Good Strength, Medium Rigidity, Good Rigidity, High Flow, High Melt, High MFI, Good Toughness, Tough, Good Processability, Easy Processing, Good Mold Release, Easy Release, Good Demolding, High Gloss, Good Chemical Resistance, Chemical Resistant.
Injection
Nominal Value
Unit
 
Drying Temperature
°F
  
Drying Time
hr
  
Suggested Max Moisture
%
  
Suggested Shot Size
%
  
Rear Temperature
°F
  
Middle Temperature
°F
  
Front Temperature
°F
  
Processing (Melt) Temp
°F
  
Mold Temperature
°F
  
Back Pressure
psi
  
Screw Speed
rpm
  
Cushion
in
  
Notes
1Typical properties: these are not to be construed as specifications.
 
IDES
Copyright © 2012 IDES
The information presented on this datasheet was acquired by IDES from the producer of the material. IDES makes substantial efforts to assure the accuracy of this data. However, IDES assumes no responsibility for the data values and strongly encourages that upon final material selection, data points are validated with the material supplier.