Radici Compounds 6020HSL

Polyamide 6

Glass Fiber Reinforcement, 20%

Supplied by Radici Plastics USA, Inc.

The technical datasheet with complete property values for Radici Compounds 6020HSL is available to members of the Prospector Plastics Database.
Register to view full datasheet.
Register to View Full Datasheet
Product Description
6020L is a nylon 6 compound reinforced with 20% glass fiber to significantly improve strength and rigidity especially at high temperatures, while maintaining good toughness. 6020L offers the high flow and easy processing that is characteristic of all nylon resins, combined with the outstanding surface gloss typical of reinforced nylon 6, and is lubricated for improved feed and mold release. For molded parts which are to be exposed to high temperature for extended periods of time, the use of 6020HSL, which contains an effective heat stabilizer package, is recommended.

Nylon 6 offers a unique combination of strength and toughness, excellent static and dynamic fatigue resistance, natural lubricity, and resistance to the effects of broad range of chemicals, oils and solvents, and is therefore used for a very wide range of applications in every end-use category.
General  
Material Status 
  • Commercial: Active
Availability 
  • North America
Filler / Reinforcement 
  • Glass Fiber Reinforcement, 20% Filler by Weight
Additive 
  • Heat Stabilizer
  • Lubricant
  
Features 
  • Fatigue Resistant
  • Good Chemical Resistance
  • Good Mold Release
  • Good Processability
  • Good Strength
  • Good Toughness
  • Heat Stabilized
  • High Flow
  • High Gloss
  • Lubricated
  • Oil Resistant
  • Solvent Resistant
Forms 
  • Pellets
Processing Method 
  • Injection Molding
Physical
Nominal Value
Unit
Test Method
Specific Gravity
 
 ASTM D792
Molding Shrinkage - Flow (0.125 in)
in/in
 ASTM D955
Water Absorption (24 hr)
%
 ASTM D570
Mechanical
Nominal Value
Unit
Test Method
Tensile Strength (Break, 73°F)
psi
 ASTM D638
Tensile Elongation (Break, 73°F)
%
 ASTM D638
Flexural Modulus (73°F)
psi
 ASTM D790
Impact
Nominal Value
Unit
Test Method
Notched Izod Impact (73°F, 0.125 in)
ft·lb/in
 ASTM D256
Hardness
Nominal Value
Unit
Test Method
Rockwell Hardness (R-Scale)
 
 ASTM D785
Thermal
Nominal Value
Unit
Test Method
Melting Temperature
°F
  
Additional Information
The value listed as Melting Point was tested in accordance with ASTM D789.
Tensile Elongation at Break, ASTM D638: 3 to 5%
Related Terminology
Product names can be difficult to match. You may have searched any one of these terms to find this product: Radici Compounds 6020HSL, Radici Compounds , RadiciCompounds6020HSL, RadiciCompounds, Compounds 6020 HSL, Compounds6020HSL, Compounds6020, Compounds, 6020 HSL, 6020HSL, Polyamide 6, Nylon 6, Polyamide, Nylon, pa6, Radici USA, Polyamide6, Nylon6, HSL6020, 6020Compounds
Generic Name
Generic Name may also be described by the following terms: PA6.
Features
Features may also be described by the following terms: Good Strength, High Flow, High Melt, High MFI, Heat Stabilized, Heat-ageing Stabilized, Heat Ageing Stabilized, Heat-aging Stabilized, Heat Aging Stabilized, Good Toughness, Tough, Good Processability, Easy Processing, Good Mold Release, Easy Release, Good Demolding, High Gloss, Good Chemical Resistance, Chemical Resistant.
Injection
Nominal Value
Unit
 
Suggested Max Moisture
%
  
Suggested Shot Size
%
  
Rear Temperature
°F
  
Middle Temperature
°F
  
Front Temperature
°F
  
Processing (Melt) Temp
°F
  
Mold Temperature
°F
  
Back Pressure
psi
  
Screw Speed
rpm
  
Cushion
in
  
Notes
1Typical properties: these are not to be construed as specifications.
 
IDES
Copyright © 2012 IDES
The information presented on this datasheet was acquired by IDES from the producer of the material. IDES makes substantial efforts to assure the accuracy of this data. However, IDES assumes no responsibility for the data values and strongly encourages that upon final material selection, data points are validated with the material supplier.