Reny 1022H Mitsubishi EP Polyarylamide (Glass Fiber Reinforcement, 50%)

General

Material Status

Commercial: Active

Availability

Asia Pacific

Europe

North America

Filler / Reinforcement

Glass Fiber Reinforcement, 50% Filler by Weight

Physical	Dry	Conditioned	Unit	Test Method
Density		--	g/cm³	ISO 1183
Melt Mass-Flow Rate (MFR) (275°C/2.16 kg)		--	g/10 min	ISO 1133
Melt Volume-Flow Rate (MVR) (275°C/2.16 kg)		--	in³/10min	ISO 1133
Molding Shrinkage		--	%
Water Absorption				ISO 62
Saturation, 73°F		--	%
Equilibrium, 73°F, 50% RH		--	%
Mechanical	Dry	Conditioned	Unit	Test Method
Tensile Modulus			psi	ISO 527-2
Tensile Stress (Break)			psi	ISO 527-2
Tensile Strain (Break)			%	ISO 527-2
Flexural Modulus			psi	ISO 178
Flexural Strength			psi	ISO 178
Impact	Dry	Conditioned	Unit	Test Method
Charpy Notched Impact Strength (73°F)			ft·lb/in²	ISO 179
Charpy Unnotched Impact Strength (73°F)			ft·lb/in²	ISO 179
Thermal	Dry	Conditioned	Unit	Test Method
Heat Deflection Temperature
66 psi, Unannealed			°F	ISO 75-2/B
264 psi, Unannealed			°F	ISO 75-2/A
CLTE				ISO 11359-2
Flow		--	in/in/°F
Transverse		--	in/in/°F
Electrical	Dry	Conditioned	Unit	Test Method
Surface Resistivity			ohms	IEC 60093
Volume Resistivity			ohm·cm	IEC 60093
Relative Permittivity				IEC 60250
100 Hz
1 MHz
Dissipation Factor				IEC 60250
100 Hz
1 MHz
Comparative Tracking Index			V	IEC 60112
Electric Strength (0.0394 in)			V/mil	IEC 60243-1
Flammability	Dry	Conditioned	Unit	Test Method
Flame Rating - UL (0.0630 in)		--		UL 94
Related Terminology
Dry	Product names can be difficult to match. You may have searched any one of these terms to find this product: Reny® 1022H, Reny 1022H, Reny® , Reny, Reny1022H, 1022 H, 1022H, Polyarylamide, PARA, Polyamide, Nylon, Mitsubishi EP, H1022
Conditioned	Product names can be difficult to match. You may have searched any one of these terms to find this product: Reny® 1022H, Reny 1022H, Reny® , Reny, Reny1022H, 1022 H, 1022H, Polyarylamide, PARA, Polyamide, Nylon, Mitsubishi EP, H1022

Injection	Dry	Unit
Drying Temperature
A		°F
B		°F
Drying Time
A		hr
B		hr
Rear Temperature		°F
Middle Temperature		°F
Front Temperature		°F
Nozzle Temperature		°F
Mold Temperature		°F
Injection Pressure		psi
Injection Rate
Screw Speed		rpm

Notes

¹Typical properties: these are not to be construed as specifications.

Reny® 1022H

Polyarylamide

Glass Fiber Reinforcement, 50%

Supplied by Mitsubishi Engineering-Plastics Corp