Density
|
|
g/cm³
|
ISO 1183 |
|
Melt Mass-Flow Rate (MFR) (190°C/2.16 kg)
|
|
g/10 min
|
ISO 1133 |
|
Tensile Modulus
|
|
psi
|
ISO 527-2 |
|
Tensile Stress (Yield)
|
|
psi
|
ISO 527-2 |
|
Film Thickness - Recommended / Available
|
|
|
|
|
Tensile Strength
|
|
|
ISO 527-3 |
|
MD: 1.2 mil, Blown Film
|
|
psi
|
|
|
TD: 1.2 mil, Blown Film
|
|
psi
|
|
|
Tensile Elongation
|
|
|
ISO 527-3 |
|
MD: Break, 1.2 mil, Blown Film
|
|
%
|
|
|
TD: Break, 1.2 mil, Blown Film
|
|
%
|
|
|
Dart Drop Impact (1.2 mil, Blown Film)
|
|
g
|
ASTM D1709 |
|
Shore Hardness (Shore D)
|
|
|
ISO 868 |
|
Ball Indentation Hardness (H 49/30)
|
|
psi
|
ISO 2039-1 |
|
Vicat Softening Temperature
|
|
°F
|
ISO 306/A50 |
|
Melting Temperature (DSC)
|
|
°F
|
ISO 3146 |
|
Gloss
|
|
|
ASTM D2457 |
|
20°, 1.18 mil
|
|
|
|
|
45°, 1.18 mil
|
|
|
|
|
60°, 1.18 mil
|
|
|
|
|
Clarity (1.18 mil)
|
|
|
ASTM D1746 |
|
Haze (1.18 mil)
|
|
%
|
ASTM D1003 |
|
Film properties tested using 30 µm thickness blown film extruded at a melt temperature of 180°C and a blow-up ratio of 2:1.
Natural Silica, ISO 3451-1: 0.1%
Erucamide, DIN 51451: 0.05%
Failure Energy, DIN 53373, 30µm: 4 J/mm
Coefficient of Friction, ISO 8295: 20%
|
|
This supplier and product may also be known by these terms: LyondellBasell Industries, Lyondell, Basell, Bassell, Basell Polyolefins, Bassel
Product names can be difficult to match. You may have searched any one of these terms to find this product: Lupolen 2426 HK, Lupolen , Lupolen2426HK, 2426 HK, 2426HK, Polyethylene, Low Density, Polyethylene Low Density, LDPE, Polyethylene, PE, LyondellBasell, PolyethyleneLowDensity, HK2426
|
|
Features may also be described by the following terms: Slip, Unspecified Slip, Good Processability, Easy Processing, Low Friction, Antiblocking, Unspecified Antiblock.
|
|
Uses may also be described by the following terms: Shrink Wrap, Rods, Rod, Food Packaging, Cast Film.
|