Specific Gravity
|
|
|
ASTM D792 |
|
Melt Mass-Flow Rate (MFR) (230°C/2.16 kg)
|
|
g/10 min
|
ASTM D1238 |
|
Molding Shrinkage - Flow (0.0787 in)
|
|
in/in
|
ASTM D955 |
|
Water Absorption (Equilibrium, 73°F, 65% RH)
|
|
%
|
ASTM D570 |
|
Tensile Strength (Yield)
|
|
psi
|
ASTM D638 |
|
Tensile Elongation (Break)
|
|
%
|
ASTM D638 |
|
Flexural Modulus
|
|
psi
|
ASTM D790 |
|
Compressive Modulus
|
|
psi
|
ASTM D695 |
|
Taber Abrasion Resistance (1000 Cycles)
|
|
mg
|
ASTM D1044 |
|
Tensile Stress (50% Strain)
|
|
psi
|
ASTM D412 |
|
Tear Strength
|
|
lbf/in
|
ASTM D624 |
|
Compression Set
|
|
%
|
ASTM D395 |
|
Notched Izod Impact
|
|
|
ASTM D256 |
|
Durometer Hardness (Shore D)
|
|
|
ASTM D2240 |
|
Deflection Temperature Under Load (264 psi, Unannealed)
|
|
°F
|
ASTM D648 |
|
Brittleness Temperature
|
|
°F
|
ASTM D746 |
|
Vicat Softening Temperature
|
|
°F
|
ASTM D1525 |
|
Melting Temperature
|
|
°F
|
DSC |
|
CLTE - Flow
|
|
in/in/°F
|
ASTM D696 |
|
Volume Resistivity
|
|
ohm·cm
|
ASTM D257 |
|
Dielectric Strength
|
|
V/mil
|
ASTM D149 |
|
Flame Rating - UL
|
|
|
UL 94 |
|
Hardness, JIS k6301, A scale: 96
10% Compression Modulus, ASTM D695: 9.2 MPa
Resilience, JIS K6301: 71 %
Brittle Point, JIS K6301: < -65 °C
Compression Set, JIS K6301: 55 %
Coefficient of Linear Thermal Expansion, TMA: 16e-5 1/K
|
|
Product names can be difficult to match. You may have searched any one of these terms to find this product: PELPRENE™ P70B, PELPRENE P70B, PELPRENE™ , PELPRENE, PELPRENEP70B, P 70 B, P70B, P70, 70B, Thermoplastic Polyester Elastomer, TPEE, Thermoplastic Elastomer, TPE, Toyobo, ThermoplasticPolyesterElastomer, ThermoplasticElastomer, 70P
|
|
Features may also be described by the following terms: Good Chemical Resistance, Chemical Resistant, Medium Heat Resistance, Good Processability, Easy Processing.
|