Specific Gravity
|
|
|
|
|
--
|
|
|
ASTM D792 |
|
--
|
|
g/cm³
|
ISO 1183 |
|
Melt Mass-Flow Rate (MFR)
|
|
g/10 min
|
ASTM D1238, ISO 1133 |
|
Molding Shrinkage - Flow
|
|
in/in
|
ASTM D955 |
|
Water Absorption (24 hr)
|
|
%
|
ASTM D570 |
|
Tensile Strength (Yield)
|
|
psi
|
ASTM D638, ISO 527-2 |
|
Tensile Elongation (Yield)
|
|
%
|
ASTM D638, ISO 527-2 |
|
Flexural Modulus
|
|
psi
|
ASTM D790, ISO 178 |
|
Notched Izod Impact Strength
|
|
ft·lb/in²
|
ISO 180 |
|
Deflection Temperature Under Load
|
|
|
|
|
66 psi, Unannealed
|
|
°F
|
ASTM D648, ISO 75-2/B |
|
264 psi, Unannealed
|
|
°F
|
ASTM D648, ISO 75-2/A |
|
Vicat Softening Temperature
|
|
|
|
|
--
|
|
°F
|
ASTM D1525 2, ISO 306/A50 2 |
|
--
|
|
°F
|
ASTM D1525 3, ISO 306/B50 3 |
|
CLTE - Flow
|
|
in/in/°F
|
ASTM D696 |
|
Volume Resistivity
|
|
ohm·cm
|
ASTM D257 |
|
Comparative Tracking Index
|
|
|
IEC 60112 |
|
Solution A
|
|
V
|
|
|
Solution B
|
|
V
|
|
|
Flame Rating - UL
|
|
|
UL 94 |
|
0.0315 in
|
|
|
|
|
0.0630 in
|
|
|
|
|
0.126 in
|
|
|
|
|
Glow Wire Ignition Temperature
|
|
°F
|
IEC 60695-2-13 |
|
Oxygen Index
|
|
%
|
ASTM D2863 |
|
Ball Penetration Test, IEC 335, 125 °C: Yes
Ball Penetration Test, IEC 335, 165 °C: No
Density, ASTM D1238: 1.1 to 1.13g/cm³
Density, ISO 1183: 1.10 to 1.13 g/cm³
Melt Flow Rate, ASTM D1238: 25 to 30 g/10 min
Melt Flow Rate, ISO 1133: 25 to 30 g/10 min
Volume Resistivity, ASTM D257: >1e15 ohm-cm
|
|
Product names can be difficult to match. You may have searched any one of these terms to find this product: DENILEN 2539, DENILEN , DENILEN2539, 2539, Polypropylene Homopolymer, PP Homopolymer, Polypropylene, PP, Vamp Tech, PolypropyleneHomopolymer, PPHomopolymer
|
|
Features may also be described by the following terms: Medium Rigidity, Good Rigidity, Good Surface Finish, High Gloss.
|