Density
|
|
g/cm³
|
ISO 1183 |
|
Melt Mass-Flow Rate (MFR) (230°C/2.16 kg)
|
|
g/10 min
|
ISO 1133 |
|
Molding Shrinkage (24 hr)
|
|
%
|
Internal Method |
|
Tensile Stress
|
|
|
ISO 527-2/5/50 |
|
Yield, 0.126 in, Injection Molded
|
|
psi
|
|
|
Break, 0.126 in, Injection Molded
|
|
psi
|
|
|
Tensile Strain (Break, 0.126 in, Injection Molded)
|
|
%
|
ISO 527-2/5/50 |
|
Flexural Modulus 2 (Injection Molded)
|
|
psi
|
ASTM D790 |
|
Charpy Notched Impact Strength (73°F, Injection Molded)
|
|
ft·lb/in²
|
ISO 179/1eA |
|
Charpy Unnotched Impact Strength (-40°F, Injection Molded)
|
|
ft·lb/in²
|
ISO 179/1eU |
|
Notched Izod Impact Strength
|
|
|
ISO 180/4A |
|
-4°F, Injection Molded
|
|
ft·lb/in²
|
|
|
32°F, Injection Molded
|
|
ft·lb/in²
|
|
|
73°F, Injection Molded
|
|
ft·lb/in²
|
|
|
Shore Hardness (Shore D, Injection Molded)
|
|
|
ISO 868 |
|
Heat Deflection Temperature (66 psi, Unannealed)
|
|
°F
|
ISO 75-2/B |
|
Vicat Softening Temperature
|
|
°F
|
ISO 306/A |
|
CLTE - Flow
|
|
|
ASTM D696 |
|
-22 to 86°F
|
|
in/in/°F
|
|
|
73 to 176°F
|
|
in/in/°F
|
|
|
Product names can be difficult to match. You may have searched any one of these terms to find this product: SABIC® PPcompound 37T1020, SABIC PPcompound 37T1020, SABIC® PPcompound , SABIC PPcompound, SABICPPcompound37T1020, SABICPPcompound, PPcompound 37 T 1020, PPcompound37T1020, PPcompound37, PPcompound, 37 T 1020, 37T1020, 37T, T1020, Polypropylene Copolymer, PP Copolymer, Polypropylene, PP, SABIC, PolypropyleneCopolymer, PPCopolymer, T37, 37PPcompound
|
|
Features may also be described by the following terms: High Flow, High Melt, High MFI, Good Stiffness, Good Impact Resistance.
|
|
Uses may also be described by the following terms: Automotive Applications, Automotive Sector.
|
|
This plastic material has approval for 2 automotive specifications from the following agencies (the number in parentheses shows the number of specifications for that agency): IMDS (1), PSA Peugeot-Citroën (1).
|