Density
|
|
g/cm³
|
ISO 1183 |
|
Melt Mass-Flow Rate (MFR)
|
|
|
ISO 1133 |
|
190°C/2.16 kg
|
|
g/10 min
|
|
|
190°C/21.6 kg
|
|
g/10 min
|
|
|
190°C/5.0 kg
|
|
g/10 min
|
|
|
Tensile Modulus (0.0787 in, Compression Molded)
|
|
psi
|
ISO 527-2/1BA/1 |
|
Tensile Stress
|
|
|
ISO 527-2/1BA/50 |
|
Yield, 0.0787 in, Compression Molded
|
|
psi
|
|
|
Break, 0.0787 in, Compression Molded
|
|
psi
|
|
|
Tensile Strain (Break, 0.0787 in, Compression Molded)
|
|
%
|
ISO 527-2/1BA/50 |
|
Notched Izod Impact Strength
|
|
|
ISO 180/1A |
|
-22°F
|
|
ft·lb/in²
|
|
|
73°F
|
|
ft·lb/in²
|
|
|
Shore Hardness (Shore D, 15 sec, Compression Molded)
|
|
|
ISO 868 |
|
Heat Deflection Temperature (66 psi, Unannealed)
|
|
°F
|
ISO 75-2/B |
|
Vicat Softening Temperature
|
|
°F
|
ISO 306/A50 |
|
Strain at Break, ISO 527, Compression Molded, Type 1BA, 50mm/min, 2mm: >1000%
Melt Flow Rate, ISO 1133, 190°C/2.16 kg: <0.1 g/10 min
ESCR, SABIC Method, Compression Molded, Determined in Rhodacal-DS10 at 75°C, 3 N/mm², thickness 1mm: 20hr
Melting Point, DIN 53765, Tmelt(top) at 5°C/min: 132°C
Enthalpy Change, DIN 53765: 205J/g
|
|
Product names can be difficult to match. You may have searched any one of these terms to find this product: SABIC® HDPE B5309, SABIC HDPE B5309, SABIC® HDPE , SABIC HDPE, SABICHDPEB5309, SABICHDPE, HDPEB 5309, HDPEB5309, HDPE, B 5309, B5309, Polyethylene, High Density, Polyethylene High Density, Polyethylene, PE, SABIC, PolyethyleneHighDensity, 5309B, 5309HDPEB
|
|
Features may also be described by the following terms: High Stiffness, Good Toughness, Tough, Good Processability, Easy Processing, Medium Molecular Weight Distribution, Wide Molecular Weight Distribution, Medium MW Distribution, Wide MW Distribution, High Environmental Stress Cracking Resistance, High ESCR, Stress Cracking Resistant.
|
|
This plastic material has 2 certifications from the following agencies (the number in parentheses shows the number of certifications for that agency): FDA (1), EEC (1).
|