Density
|
|
g/cm³
|
ISO 1183 |
|
Melt Mass-Flow Rate (MFR)
|
|
|
ISO 1133 |
|
190°C/2.16 kg
|
|
g/10 min
|
|
|
190°C/5.0 kg
|
|
g/10 min
|
|
|
Tensile Modulus (0.0787 in, Compression Molded)
|
|
psi
|
ISO 527-2/1BA/1 |
|
Tensile Stress
|
|
|
ISO 527-2/1BA/50 |
|
Yield, 0.0787 in, Compression Molded
|
|
psi
|
|
|
Break, 0.0787 in, Compression Molded
|
|
psi
|
|
|
Tensile Strain (Break, 0.0787 in, Compression Molded)
|
|
%
|
ISO 527-2/1BA/50 |
|
Notched Izod Impact Strength
|
|
|
ISO 180/1A |
|
-22°F
|
|
ft·lb/in²
|
|
|
73°F
|
|
ft·lb/in²
|
|
|
Shore Hardness (Shore D, 15 sec, Compression Molded)
|
|
|
ISO 868 |
|
Heat Deflection Temperature
|
|
|
|
|
66 psi, Unannealed
|
|
°F
|
ISO 75-2/B |
|
264 psi, Unannealed
|
|
°F
|
ISO 75-2/A |
|
Vicat Softening Temperature
|
|
|
|
|
--
|
|
°F
|
ISO 306/A50 |
|
--
|
|
°F
|
ISO 306/B50 |
|
Strain at Break, ISO 527, Compression Molded, Type 1BA, 50mm/min, 2mm: >2000%
ESCR, SABIC Method, Compression Molded, Determined in Rhodacal-DS10 at 75°C, 3 N/mm², thickness 1mm: 100hr
Melting Point, DIN 53765, Tmelt(top) at 5°C/min: 134°C
Enthalpy Change, DIN 53765: 215J/g
|
|
Product names can be difficult to match. You may have searched any one of these terms to find this product: SABIC® Vestolen A 6012, SABIC Vestolen A 6012, SABIC® Vestolen A , SABIC Vestolen A, SABICVestolenA6012, SABICVestolenA, A 6012, A6012, 6012, Polyethylene, High Density, Polyethylene High Density, HDPE, Polyethylene, PE, SABIC, PolyethyleneHighDensity, 6012A
|
|
Features may also be described by the following terms: Low Warpage, Low Warp, High Purity, Good Processability, Easy Processing, Narrow Molecular Weight Distribution, Narrow MW Distribution.
|
|
This plastic material has 2 certifications from the following agencies (the number in parentheses shows the number of certifications for that agency): FDA (1), EEC (1).
|