Density
|
|
g/cm³
|
ISO 1183 |
|
Melt Mass-Flow Rate (MFR)
|
|
|
ISO 1133 |
|
190°C/2.16 kg
|
|
g/10 min
|
|
|
190°C/5.0 kg
|
|
g/10 min
|
|
|
Melt Volume-Flow Rate (MVR)
|
|
|
ISO 1133 |
|
190°C/2.16 kg
|
|
in³/10min
|
|
|
190°C/5.0 kg
|
|
in³/10min
|
|
|
Tensile Modulus (0.0787 in, Compression Molded)
|
|
psi
|
ISO 527-2/1BA/1 |
|
Tensile Stress
|
|
|
ISO 527-2/1BA/50 |
|
Yield, 0.0787 in, Compression Molded
|
|
psi
|
|
|
Break, 0.0787 in, Compression Molded
|
|
psi
|
|
|
Tensile Strain (Break, 0.0787 in, Compression Molded)
|
|
%
|
ISO 527-2/1BA/50 |
|
Tensile Creep Modulus
|
|
|
ISO 899-1 |
|
1 hr
|
|
psi
|
|
|
1000 hr
|
|
psi
|
|
|
Notched Izod Impact Strength
|
|
|
ISO 180/1A |
|
-22°F
|
|
ft·lb/in²
|
|
|
73°F
|
|
ft·lb/in²
|
|
|
Tensile Impact Strength
|
|
ft·lb/in²
|
ISO 8256/1B |
|
Shore Hardness (Shore D, 15 sec, Compression Molded)
|
|
|
ISO 868 |
|
Ball Indentation Hardness (H 132/30)
|
|
psi
|
ISO 2039-1 |
|
Heat Deflection Temperature
|
|
|
|
|
66 psi, Unannealed
|
|
°F
|
ISO 75-2/B |
|
264 psi, Unannealed
|
|
°F
|
ISO 75-2/A |
|
Vicat Softening Temperature
|
|
|
|
|
--
|
|
°F
|
ISO 306/A50 |
|
--
|
|
°F
|
ISO 306/B50 |
|
ESCR, SABIC Method, Determined in Rhodacal-DS10 at 60°C, 2 N/mm², thickness 3mm: 30hr
Tensile Impact Elongation at Break, ISO 8256, Type 1, Method B: 1.4%
Tensile Impact Maximum Tension, ISO 8256, Type 1, Method B: 34 MPa
Melting Point, DIN 53765, Tmelt(top) at 5°C/min: 130°C
Enthalpy Change, DIN 53765: 200J/g
|
|
Product names can be difficult to match. You may have searched any one of these terms to find this product: SABIC® HDPE M100053C, SABIC HDPE M100053C, SABIC® HDPE , SABIC HDPE, SABICHDPEM100053C, SABICHDPE, HDPEM 100053 C, HDPEM100053C, HDPEM100053, HDPE, M 100053 C, M100053C, M100053, 100053C, Polyethylene, High Density, Polyethylene High Density, Polyethylene, PE, SABIC, PolyethyleneHighDensity, 100053M, 100053HDPEM
|
|
Features may also be described by the following terms: Good Organoleptic Properties, Good Toughness, Tough, High Purity, Good Processability, Easy Processing, Narrow Molecular Weight Distribution, Narrow MW Distribution, High Environmental Stress Cracking Resistance, High ESCR, Stress Cracking Resistant.
|
|
Uses may also be described by the following terms: Closure Caps, Caps, Cap.
|
|
This plastic material has 2 certifications from the following agencies (the number in parentheses shows the number of certifications for that agency): FDA (1), EEC (1).
|