Density
|
|
g/cm³
|
ISO 1183 |
|
Melt Mass-Flow Rate (MFR)
|
|
|
ISO 1133 |
|
190°C/2.16 kg
|
|
g/10 min
|
|
|
190°C/5.0 kg
|
|
g/10 min
|
|
|
Tensile Modulus (0.0787 in, Compression Molded)
|
|
psi
|
ISO 527-2/1BA/1 |
|
Tensile Stress
|
|
|
ISO 527-2/1BA/50 |
|
Yield, 0.0787 in, Compression Molded
|
|
psi
|
|
|
Break, 0.0787 in, Compression Molded
|
|
psi
|
|
|
Tensile Strain (Break, 0.0787 in, Compression Molded)
|
|
%
|
ISO 527-2/1BA/50 |
|
Tensile Creep Modulus
|
|
|
ISO 899-1 |
|
1 hr
|
|
psi
|
|
|
1000 hr
|
|
psi
|
|
|
Notched Izod Impact Strength
|
|
|
ISO 180/1A |
|
-22°F
|
|
ft·lb/in²
|
|
|
73°F
|
|
ft·lb/in²
|
|
|
Tensile Impact Strength
|
|
ft·lb/in²
|
ISO 8256/1B |
|
Shore Hardness (Shore D, 15 sec, Compression Molded)
|
|
|
ISO 868 |
|
Ball Indentation Hardness (H 132/30)
|
|
psi
|
ISO 2039-1 |
|
Heat Deflection Temperature
|
|
|
|
|
66 psi, Unannealed
|
|
°F
|
ISO 75-2/B |
|
264 psi, Unannealed
|
|
°F
|
ISO 75-2/A |
|
Vicat Softening Temperature
|
|
|
|
|
--
|
|
°F
|
ISO 306/A50 |
|
--
|
|
°F
|
ISO 306/B50 |
|
ESCR, SABIC Method, Determined in Rhodacal-DS10 at 60°C, 2 N/mm², thickness 3mm: 100hr
Tensile Impact Elongation at Break, ISO 8256, Type 1, Method B: 1.8%
Tensile Impact Maximum Tension, ISO 8256, Type 1, Method B: 31 MPa
Melting Point, DIN 53765, Tmelt(top) at 5°C/min: 131°C
Enthalpy Change, DIN 53765: 205J/g
|
|
Product names can be difficult to match. You may have searched any one of these terms to find this product: SABIC® HDPE M40053, SABIC HDPE M40053, SABIC® HDPE , SABIC HDPE, SABICHDPEM40053, SABICHDPE, HDPEM 40053, HDPEM40053, HDPE, M 40053, M40053, Polyethylene, High Density, Polyethylene High Density, Polyethylene, PE, SABIC, PolyethyleneHighDensity, 40053M, 40053HDPEM
|
|
Features may also be described by the following terms: High Purity, Low Warpage, Low Warp, Low Temperatuer Impact Resistance, Low Temp Impact Resistance, High Impact Resistance, Narrow Molecular Weight Distribution, Narrow MW Distribution, High Environmental Stress Cracking Resistance, High ESCR, Stress Cracking Resistant, Good Processability, Easy Processing.
|
|
This plastic material has 2 certifications from the following agencies (the number in parentheses shows the number of certifications for that agency): FDA (1), EEC (1).
|