SABIC LDPE 2101TN00 SABIC Polyethylene, Low Density

Product Description

SABIC® LDPE 2101TN00 is a grade with good toughness and good biaxial shrink properties. The material contains no additives, has a low energy consumption during processing and a good draw down ability.

SABIC® LDPE 2101TN00 is very suitable for thin shrink film.

General

Material Status

Commercial: Active

Availability

Europe

Features

Foamable

Good Drawdown

Good Toughness

Uses

Film

Foam

Shrink Wrap

Forms

Pellets

Processing Method

Blown Film

Physical	Nominal Value	Unit	Test Method
Density		g/cm³	ISO 1183/A
Melt Mass-Flow Rate (MFR) (190°C/2.16 kg)		g/10 min	ISO 1133
Mechanical	Nominal Value	Unit	Test Method
Coefficient of Friction (Blown Film)			ASTM D1894
Films	Nominal Value	Unit	Test Method
Tensile Modulus			ISO 527-3
MD: 2.0 mil, Blown Film		psi
TD: 2.0 mil, Blown Film		psi
Tensile Stress			ISO 527-3
MD: Yield, 2.0 mil, Blown Film		psi
TD: Yield, 2.0 mil, Blown Film		psi
MD: 2.0 mil, Blown Film		psi
TD: 2.0 mil, Blown Film		psi
Tensile Elongation			ISO 527-3
MD: Break, 2.0 mil, Blown Film		%
TD: Break, 2.0 mil, Blown Film		%
Hardness	Nominal Value	Unit	Test Method
Shore Hardness (Shore D, Compression Molded)			ISO 868
Thermal	Nominal Value	Unit	Test Method
Vicat Softening Temperature		°F	ISO 306/A50
Melting Temperature (DSC)		°F	ISO 3146
Peak Crystallization Temperature (DSC)		°F	ISO 3146
Optical	Nominal Value	Unit	Test Method
Haze (1.97 mil, Blown Film)		%	ASTM D1003
Additional Information
50µm blown film processed with a blow up ratio of 3:1 and a die gap of 0.8 mm. Modulus of Elasticity, SABIC Method: 250 MPa Melting Point, SABIC Method, DSC: 110°C Crystallization Temperature, SABIC Method, DSC: 97°C Average Heat of Fusion, SABIC Method, DSC: 110 J/g Clarity, SABIC Method, Blown Film, 50µm: 30mV Blocking, SABIC Method, Blown Film: 50g Re-blocking, SABIC Method, Blown Film: 50g Impact Strength, ASTM D4272, 50µm, Blown Film: 25 kJ/m Tear Strength, ISO 6383-2, 50µm, Blown Film, TD: 30 kN/m Tear Strength, ISO 6383-2, 50µm, Blown Film, MD: 40 kN/m Vicat Softening Temperature, ISO 306, Foam extrusion, A50 (50°C/h 10N): 90°C
Related Terminology
Product names can be difficult to match. You may have searched any one of these terms to find this product: SABIC® LDPE 2101TN00, SABIC LDPE 2101TN00, SABIC® LDPE , SABIC LDPE, SABICLDPE2101TN00, SABICLDPE, LDPE 2101 TN 00, LDPE2101TN00, LDPE2101, LDPE, 2101 TN 00, 2101TN00, 2101TN, TN00, Polyethylene, Low Density, Polyethylene Low Density, Polyethylene, PE, SABIC, PolyethyleneLowDensity, TN2101, 2101LDPE
Features
Features may also be described by the following terms: Good Drawdown, Good draw down, Good Toughness, Tough.
Uses
Uses may also be described by the following terms: Shrink Wrap.

Notes

¹Typical properties: these are not to be construed as specifications.

SABIC® LDPE 2101TN00

Low Density Polyethylene

Supplied by Saudi Basic Industries Corporation (SABIC)