Density
|
|
g/cm³
|
ISO 1183/A |
|
Melt Mass-Flow Rate (MFR) (190°C/2.16 kg)
|
|
g/10 min
|
ISO 1133 |
|
Coefficient of Friction (Blown Film)
|
|
|
ASTM D1894 |
|
Tensile Modulus
|
|
|
ISO 527-3 |
|
MD: 0.98 mil, Cast Film
|
|
psi
|
|
|
TD: 0.98 mil, Cast Film
|
|
psi
|
|
|
MD: 2.0 mil, Blown Film
|
|
psi
|
|
|
TD: 2.0 mil, Blown Film
|
|
psi
|
|
|
Tensile Stress
|
|
|
ISO 527-3 |
|
MD: Yield, 0.98 mil, Cast Film
|
|
psi
|
|
|
TD: Yield, 0.98 mil, Cast Film
|
|
psi
|
|
|
MD: Yield, 2.0 mil, Blown Film
|
|
psi
|
|
|
TD: Yield, 2.0 mil, Blown Film
|
|
psi
|
|
|
MD: 0.98 mil, Cast Film
|
|
psi
|
|
|
TD: 0.98 mil, Cast Film
|
|
psi
|
|
|
MD: 2.0 mil, Blown Film
|
|
psi
|
|
|
TD: 2.0 mil, Blown Film
|
|
psi
|
|
|
Tensile Elongation
|
|
|
ISO 527-3 |
|
MD: Break, 0.98 mil, Cast Film
|
|
%
|
|
|
TD: Break, 0.98 mil, Cast Film
|
|
%
|
|
|
MD: Break, 2.0 mil, Blown Film
|
|
%
|
|
|
TD: Break, 2.0 mil, Blown Film
|
|
%
|
|
|
Shore Hardness (Shore D, Compression Molded)
|
|
|
ISO 868 |
|
Vicat Softening Temperature
|
|
°F
|
ISO 306/A50 |
|
Haze
|
|
|
ASTM D1003 |
|
1.77 mil, Blown Film
|
|
%
|
|
|
0.984 mil, Cast Film
|
|
%
|
|
|
50µm blown film processed with a blow up ratio of 3:1 and a die gap of 0.8 mm.
25µm cast film processed with a die gap of 1.0 mm.
Modulus of Elasticity, SABIC Method: 320 MPa
Melting Point, SABIC Method, DSC: 113°C
Crystallization Temperature, SABIC Method, DSC: 100°C
Average Heat of Fusion, SABIC Method, DSC: 123 J/g
Clarity, SABIC Method, Blown Film, 45µm: 34mV
Clarity, SABIC Method, Cast Film, 25µm: 23mV
Blocking, SABIC Method, Blown Film: 20g
Re-blocking, SABIC Method, Blown Film: <5g
Impact Strength, ASTM D4272, 50µm, Blown Film: 15 kJ/m
Tear Strength, ISO 6383-2, 50µm, Blown Film, TD: 45 kN/m
Tear Strength, ISO 6383-2, 50µm, Blown Film, MD: 45 kN/m
Impact Strength, ASTM D4272, 25µm, Cast Film: 14 kJ/m
|
|
Product names can be difficult to match. You may have searched any one of these terms to find this product: SABIC® LDPE 2501TN00, SABIC LDPE 2501TN00, SABIC® LDPE , SABIC LDPE, SABICLDPE2501TN00, SABICLDPE, LDPE 2501 TN 00, LDPE2501TN00, LDPE2501, LDPE, 2501 TN 00, 2501TN00, 2501TN, TN00, Polyethylene, Low Density, Polyethylene Low Density, Polyethylene, PE, SABIC, PolyethyleneLowDensity, TN2501, 2501LDPE
|
|
Features may also be described by the following terms: Good Processability, Easy Processing, Good Stiffness, Good Drawdown, Good draw down.
|
|
Uses may also be described by the following terms: Cast Film.
|