Density
|
|
g/cm³
|
ISO 1183/A |
|
Melt Mass-Flow Rate (MFR) (190°C/2.16 kg)
|
|
g/10 min
|
ISO 1133 |
|
Coefficient of Friction (Blown Film)
|
|
|
ASTM D1894 |
|
Tensile Modulus
|
|
|
ISO 527-3 |
|
MD: 2.0 mil, Blown Film
|
|
psi
|
|
|
TD: 2.0 mil, Blown Film
|
|
psi
|
|
|
Tensile Stress
|
|
|
ISO 527-3 |
|
MD: Yield, 2.0 mil, Blown Film
|
|
psi
|
|
|
TD: Yield, 2.0 mil, Blown Film
|
|
psi
|
|
|
MD: 1.8 mil, Blown Film
|
|
psi
|
|
|
TD: 1.8 mil, Blown Film
|
|
psi
|
|
|
Tensile Elongation
|
|
|
ISO 527-3 |
|
MD: Break, 2.0 mil, Blown Film
|
|
%
|
|
|
TD: Break, 2.0 mil, Blown Film
|
|
%
|
|
|
Vicat Softening Temperature
|
|
°F
|
ISO 306/A50 |
|
Gloss (45°, 1.97 mil, Blown Film)
|
|
|
ASTM D2457 |
|
Haze (1.97 mil, Blown Film)
|
|
%
|
ASTM D1003 |
|
50µm blown film processed with a blow up ratio of 3:1 and a die gap of 0.8 mm.
Clarity, SABIC Method, Blown Film, 50µm: 25mV
Blocking, SABIC Method, Blown Film: 20g
Re-blocking, SABIC Method, Blown Film: <5g
Impact Strength, ASTM D4272, 50µm, Blown Film: 25 kJ/m
Tear Strength, ISO 6383-2, 50µm, Blown Film, TD: 45 kN/m
Tear Strength, ISO 6383-2, 50µm, Blown Film, MD: 35 kN/m
|
|
Product names can be difficult to match. You may have searched any one of these terms to find this product: SABIC® LDPE 2600TC00, SABIC LDPE 2600TC00, SABIC® LDPE , SABIC LDPE, SABICLDPE2600TC00, SABICLDPE, LDPE 2600 TC 00, LDPE2600TC00, LDPE2600, LDPE, 2600 TC 00, 2600TC00, 2600TC, TC00, Polyethylene, Low Density, Polyethylene Low Density, Polyethylene, PE, SABIC, PolyethyleneLowDensity, TC2600, 2600LDPE
|
|