Density
|
|
g/cm³
|
ISO 1183 |
|
Melt Mass-Flow Rate (MFR)
|
|
|
ISO 1133 |
|
190°C/2.16 kg
|
|
g/10 min
|
|
|
190°C/5.0 kg
|
|
g/10 min
|
|
|
Melt Volume-Flow Rate (MVR)
|
|
|
ISO 1133 |
|
190°C/2.16 kg
|
|
in³/10min
|
|
|
190°C/5.0 kg
|
|
in³/10min
|
|
|
Environmental Stress-Cracking Resistance 2 (140°F, 0.0787 in, Compression Molded)
|
|
hr
|
Internal Method |
|
Tensile Modulus (0.0787 in, Compression Molded)
|
|
psi
|
ISO 527-2/1BA/50 |
|
Tensile Stress
|
|
|
|
|
Yield, 0.0630 in, Compression Molded
|
|
psi
|
ISO 527-2/200 |
|
Yield, 0.0787 in, Compression Molded
|
|
psi
|
ISO 527-2/1BA/50 |
|
Break, 0.0630 in, Compression Molded
|
|
psi
|
ISO 527-2/200 |
|
Break, 0.0787 in, Compression Molded
|
|
psi
|
ISO 527-2/1BA/50 |
|
Tensile Strain
|
|
|
|
|
Break, 0.0630 in, Compression Molded
|
|
%
|
ISO 527-2/200 |
|
Break, 0.0787 in, Compression Molded
|
|
%
|
ISO 527-2/1BA/50 |
|
Tensile Creep Modulus
|
|
|
ISO 899-1 |
|
1 hr
|
|
psi
|
|
|
1000 hr
|
|
psi
|
|
|
Film Thickness - Tested
|
|
mil
|
|
|
Tensile Stress
|
|
|
ISO 527-3 |
|
MD: Yield, 0.98 mil
|
|
psi
|
|
|
TD: Yield, 0.98 mil
|
|
psi
|
|
|
MD: 0.98 mil
|
|
psi
|
|
|
TD: 0.98 mil
|
|
psi
|
|
|
Tensile Elongation
|
|
|
ISO 527-3 |
|
MD: Break, 0.98 mil
|
|
%
|
|
|
TD: Break, 0.98 mil
|
|
%
|
|
|
Water Vapor Transmission Rate (100°F, 0.98 mil, 100% RH)
|
|
g/100 in²/24 hr
|
Internal Method |
|
Oxygen Permeability 3 (73°F, 1.0 mil)
|
|
cm³/cm²/bar/24 hr
|
Internal Method |
|
Notched Izod Impact Strength
|
|
|
ISO 180/A |
|
-22°F
|
|
ft·lb/in²
|
|
|
73°F
|
|
ft·lb/in²
|
|
|
Shore Hardness (Shore D)
|
|
|
ISO 868 |
|
Heat Deflection Temperature (66 psi, Unannealed)
|
|
°F
|
ISO 75-2/B |
|
Vicat Softening Temperature
|
|
°F
|
ISO 306/A50 |
|
Melting Temperature (DSC)
|
|
°F
|
DIN 53765 |
|
Enthalpy Change
|
|
J/g
|
DIN 53765 |
|
Flexural Crack Resistance (1.0 mil)
|
|
cycles/10 holes
|
Internal Method |
|
Tear Strength
|
|
|
ISO 6383-2 |
|
MD: 1.0 mil
|
|
lbf/in
|
|
|
TD: 1.0 mil
|
|
lbf/in
|
|
|
Product names can be difficult to match. You may have searched any one of these terms to find this product: SABIC® LDPE 1808AN00, SABIC LDPE 1808AN00, SABIC® LDPE , SABIC LDPE, SABICLDPE1808AN00, SABICLDPE, LDPE 1808 AN 00, LDPE1808AN00, LDPE1808, LDPE, 1808 AN 00, 1808AN00, 1808AN, AN00, Polyethylene, Low Density, Polyethylene Low Density, Polyethylene, PE, SABIC, PolyethyleneLowDensity, AN1808, 1808LDPE
|
|
Features may also be described by the following terms: Good Drawdown, Good draw down, Low Gel, High Environmental Stress Cracking Resistance, High ESCR, Stress Cracking Resistant, Good Flexibility, Flexible, Wide Molecular Weight Distribution, Wide MW Distribution, Broad Molecular Weight Distribution, Ultra High Toughness.
|
|
Uses may also be described by the following terms: Compounding, Compounds.
|
|
This plastic material has 2 certifications from the following agencies (the number in parentheses shows the number of certifications for that agency): FDA (1), EEC (1).
|