Density
|
|
g/cm³
|
ISO 1183 |
|
Melt Mass-Flow Rate (MFR)
|
|
|
ISO 1133 |
|
190°C/2.16 kg
|
|
g/10 min
|
|
|
190°C/5.0 kg
|
|
g/10 min
|
|
|
Melt Volume-Flow Rate (MVR)
|
|
|
ISO 1133 |
|
190°C/2.16 kg
|
|
in³/10min
|
|
|
190°C/5.0 kg
|
|
in³/10min
|
|
|
Tensile Modulus (0.0787 in, Compression Molded)
|
|
psi
|
ISO 527-2/1BA/50 |
|
Tensile Stress
|
|
|
ISO 527-2/1BA/50 |
|
Yield, 0.0787 in, Compression Molded
|
|
psi
|
|
|
Break, 0.0787 in, Compression Molded
|
|
psi
|
|
|
Tensile Strain (Break, 0.0787 in, Compression Molded)
|
|
%
|
ISO 527-2/1BA/50 |
|
Tensile Creep Modulus
|
|
|
ISO 899-1 |
|
1 hr
|
|
psi
|
|
|
1000 hr
|
|
psi
|
|
|
Notched Izod Impact Strength (73°F)
|
|
ft·lb/in²
|
ISO 180/1A |
|
Tensile Impact Strength
|
|
ft·lb/in²
|
ISO 8256/1B |
|
Shore Hardness (Shore D, 15 sec, Compression Molded)
|
|
|
ISO 868 |
|
Ball Indentation Hardness (H 49/30)
|
|
psi
|
ISO 2039-1 |
|
Heat Deflection Temperature (66 psi, Unannealed)
|
|
°F
|
ISO 75-2/B |
|
Vicat Softening Temperature
|
|
°F
|
ISO 306/A50 |
|
Modulus of Elasticity, SABIC Method: 300 MPa
Melting Point, SABIC Method, DSC: 109°C
Crystallization Temperature, SABIC Method, DSC: 98°C
Average Heat of Fusion, SABIC Method, DSC: 115 J/g
ESCR, SABIC Method, Determined in Rhodacal-DS10 at 60°C, 2 N/mm², thickness 3mm: 40hr
Tensile Impact Elongation at Break, ISO 8256, Type 1, Method B: 8.4%
Tensile Impact Maximum Tension, ISO 8256, Type 1, Method B: 19 MPa
Melting Point, DIN 53765, Tmelt(top) at 5°C/min: 109°C
Enthalpy Change, DIN 53765: 115J/g
|
|
Product names can be difficult to match. You may have searched any one of these terms to find this product: SABIC® LDPE 2308AN00, SABIC LDPE 2308AN00, SABIC® LDPE , SABIC LDPE, SABICLDPE2308AN00, SABICLDPE, LDPE 2308 AN 00, LDPE2308AN00, LDPE2308, LDPE, 2308 AN 00, 2308AN00, 2308AN, AN00, Polyethylene, Low Density, Polyethylene Low Density, Polyethylene, PE, SABIC, PolyethyleneLowDensity, AN2308, 2308LDPE
|
|
Features may also be described by the following terms: High Flow, High Melt, High MFI.
|
|
This plastic material has 2 certifications from the following agencies (the number in parentheses shows the number of certifications for that agency): FDA (1), EEC (1).
|