Impet 2700 GV1/45 (Europe) Ticona Polyethylene Terephthalate (Glass Fiber Reinforcement, 45%)

Product Description

Chemical abbreviation according to ISO 1043-1: PET
Moulding compound ISO 7792- PET, MGHR, 08-160, GF45

Polyethylene terephthalate, 45 % glass fibre reinforced, high
flowability, excellent gloss, high modulus, very high heat deflection
temperature.

Injection mould temperature 135-145 °C.

General

Material Status

Commercial: Active

Availability

Europe

Filler / Reinforcement

Glass Fiber Reinforcement, 45% Filler by Weight

Features

High Flow

High Gloss

High Stiffness

RoHS Compliance

Processing Method

Injection Molding

Multi-Point Data

Isochronous Stress vs. Strain (ISO 11403-1)

Isothermal Stress vs. Strain (ISO 11403-1)

Resin ID (ISO 1043)

Physical	Nominal Value	Unit	Test Method
Density		g/cm³	ISO 1183
Water Absorption (Equilibrium, 73°F, 50% RH)		%	ISO 62
Viscosity Number		cm³/g	ISO 307
Mechanical	Nominal Value	Unit	Test Method
Tensile Modulus		psi	ISO 527-2/1A/1
Tensile Stress (Break)		psi	ISO 527-2/1A/5
Tensile Strain (Break)		%	ISO 527-2/1A/5
Flexural Strength (73°F)		psi	ISO 178
Impact	Nominal Value	Unit	Test Method
Charpy Notched Impact Strength			ISO 179/1eA
-22°F		ft·lb/in²
73°F		ft·lb/in²
Charpy Unnotched Impact Strength			ISO 179/1eU
-22°F		ft·lb/in²
73°F		ft·lb/in²
Thermal	Nominal Value	Unit	Test Method
Heat Deflection Temperature
264 psi, Unannealed		°F	ISO 75-2/A
1160 psi, Unannealed		°F	ISO 75-2/C
Vicat Softening Temperature		°F	ISO 306/B50
Melting Temperature²		°F	ISO 11357-3
CLTE - Flow		in/in/°F	ISO 11359-2
Electrical	Nominal Value	Unit	Test Method
Surface Resistivity		ohms	IEC 60093
Volume Resistivity		ohm·cm	IEC 60093
Relative Permittivity			IEC 60250
100 Hz
1 MHz
Dissipation Factor			IEC 60250
100 Hz
1 MHz
Comparative Tracking Index		V	IEC 60112
Electric Strength		V/mil	IEC 60243-1
Flammability	Nominal Value	Unit	Test Method
Flame Rating - UL			UL 94
0.0315 in
0.0630 in
Oxygen Index		%	ISO 4589-2
Additional Information	Nominal Value	Unit	Test Method
ISO Type			ISO 7792
Related Terminology
Product names can be difficult to match. You may have searched any one of these terms to find this product: Impet® 2700 GV1/45, Impet 2700 GV1 45, Impet® 2700 GV1/45 (Europe), Impet 2700 GV145 Europe, Impet® , Impet, Impet2700GV145Europe, 2700 GV 1 45, 2700 GV 1, 2700 GV145, 2700 GV1, 2700 GV1/45, 2700 GV1 45, 2700 GV 1 45 Europe, 2700GV145, 2700GV1, 2700 GV1/45 (Europe), 2700 GV145 Europe, 2700 GV1:45 (Europe), 2700 GV1:45, 2700 GV1+45 (Europe), 2700 GV1+45, 2700 GV1-45 (Europe), 2700 GV1-45, 2700 GV1_45 (Europe), 2700 GV1_45, 2700 GV1 45 (Europe), 2700GV, GV1, 145, 45Europe, 2700GV1_45, 2700GV145Europe, 2700 GV1_45 Europe, 2700 GV1 45 Europe, 2700GV1_45Europe, Polyethylene Terephthalate, PET, Polyester, Ticona, PolyethyleneTerephthalate, GV2700
Features
Features may also be described by the following terms: High Gloss, High Flow, High Melt, High MFI, High Stiffness.

Injection	Nominal Value	Unit
Processing (Melt) Temp		°F
Mold Temperature		°F
Injection Pressure		psi
Injection Rate
Holding Pressure		psi
Back Pressure		psi
Injection Notes
Maximum Barrel Residence Time: 5 to 10 min Peripheral Screw Speed: max. 0.3 m/s Nozzle Design: open design preferred Injection speed, injection pressure and holding pressure have to be optimized to the individual article geometry. To avoid material degradation during processing low back pressure and minimum screw speed have to be used. Overheating of the material has to be avoided. Ticona recommends only externally heated hot runner systems. ) For moulded parts with especially high requirements to the surface quality or dimensional stability, a mold temperature of up to 110°C can be advantageous. *) If the cylinder temperatures are higher than the recommended maximum temperatures, the max. residence time in the barrel has to be reduced.

Notes

¹Typical properties: these are not to be construed as specifications.

²10°C/min

Impet® 2700 GV1/45 (Europe)

Polyethylene Terephthalate

Glass Fiber Reinforcement, 45%

Supplied by Ticona