Density
|
|
g/cm³
|
ISO 1183 |
|
Melt Mass-Flow Rate (MFR)
|
|
|
ISO 1133 |
|
230°C/2.16 kg
|
|
g/10 min
|
|
|
230°C/5.0 kg
|
|
g/10 min
|
|
|
Molding Shrinkage
|
|
%
|
ISO 294-4 |
|
Tensile Modulus (Injection Molded)
|
|
psi
|
ISO 527-2/1 |
|
Tensile Stress (Yield, Injection Molded)
|
|
psi
|
ISO 527-2/50 |
|
Tensile Strain (Yield, Injection Molded)
|
|
%
|
ISO 527-2/50 |
|
Flexural Modulus 2 (Injection Molded)
|
|
psi
|
ISO 178 |
|
Charpy Notched Impact Strength
|
|
|
ISO 179/1eA |
|
-4°F
|
|
ft·lb/in²
|
|
|
73°F
|
|
ft·lb/in²
|
|
|
Charpy Unnotched Impact Strength
|
|
|
ISO 179/1eU |
|
-4°F
|
|
ft·lb/in²
|
|
|
73°F
|
|
ft·lb/in²
|
|
|
Ball Indentation Hardness (H 358/30)
|
|
psi
|
ISO 2039-1 |
|
Heat Deflection Temperature
|
|
|
|
|
66 psi, Unannealed
|
|
°F
|
ISO 75-2/B |
|
264 psi, Unannealed
|
|
°F
|
ISO 75-2/A |
|
Vicat Softening Temperature
|
|
|
|
|
--
|
|
°F
|
ISO 306/A50 |
|
--
|
|
°F
|
ISO 306/B50 |
|
The value listed as Molding Shrinkage, ISO 294-4, was tested in accordance with Borealis test methods.
Fogging, DIN 75201, 100°C, 3 hr: 88.3%
Fogging, DIN 75201, 100°C, 16 hr: 0.4mg
Emission, VDA 277: 27 µg C/g
|
|
Product names can be difficult to match. You may have searched any one of these terms to find this product: Daplen™ ED224T, Daplen ED224T, Daplen™ , Daplen, DaplenED224T, ED 224 T, ED224T, ED224, 224T, Polypropylene, Unspecified, Polypropylene Unspecified, PP, Unspecified, PP Unspecified, Polypropylene, PP, Borealis, PolypropyleneUnspecified, PPUnspecified, 224ED
|
|
Generic Name may also be described by the following terms: Polypropilene, Polypropelene.
|
|
Features may also be described by the following terms: Good Stiffness, Good Impact Resistance, Heat Stabilized, Heat-ageing Stabilized, Heat Ageing Stabilized, Heat-aging Stabilized, Heat Aging Stabilized.
|
|
Uses may also be described by the following terms: Automotive Applications, Automotive Sector.
|