AT 525 Celanese EVA Polyethylene, Low Density

Product Description

A high strength resin, recommended for shrink films and general purpose packaging.

General

Material Status

Availability

Features

Uses

Forms

Processing Method

Physical	Nominal Value	Unit	Test Method
Density		g/cm³	ASTM D1505
Melt Mass-Flow Rate (MFR) (190°C/2.16 kg)		g/10 min	ASTM D1238
Mechanical	Nominal Value	Unit	Test Method
Coefficient of Friction (Blown Film)			ASTM D1894
Films	Nominal Value	Unit	Test Method
Film Thickness - Tested		mil
Secant Modulus			ASTM D882
1% Secant, MD: 1.4 mil, Blown Film		psi
1% Secant, TD: 1.4 mil, Blown Film		psi
Tensile Strength²			ASTM D882A
MD: Yield, 1.4 mil, Blown Film		psi
TD: Yield, 1.4 mil, Blown Film		psi
MD: Break, 1.4 mil, Blown Film		psi
TD: Break, 1.4 mil, Blown Film		psi
Tensile Elongation²			ASTM D882A
MD: Break, 1.4 mil, Blown Film		%
TD: Break, 1.4 mil, Blown Film		%
Dart Drop Impact (1.4 mil, Blown Film)		g	ASTM D1709
Thermal	Nominal Value	Unit	Test Method
Vicat Softening Temperature		°F	ASTM D1525
Optical	Nominal Value	Unit	Test Method
Gloss (45°, 1.38 mil, Blown Film)			ASTM D2457
Haze (1.38 mil, Blown Film)		%	ASTM D1003
Related Terminology
Product names can be difficult to match. You may have searched any one of these terms to find this product: AT 525, AT , AT525, 525, Polyethylene, Low Density, Polyethylene Low Density, LDPE, Polyethylene, PE, Celanese EVA, PolyethyleneLowDensity
Features
Features may also be described by the following terms: High Strength.
Uses
Uses may also be described by the following terms: Shrink Wrap.

Extrusion	Nominal Value	Unit
Melt Temperature		°F

Notes

¹Typical properties: these are not to be construed as specifications.

²20 in/min

AT 525