Density
|
|
--
|
g/cm³
|
ISO 1183 |
|
Molding Shrinkage - Flow
|
|
--
|
%
|
ISO 294-4 |
|
Water Absorption (73°F, 24 hr)
|
|
--
|
%
|
ISO 62 |
|
Tensile Modulus
|
|
|
psi
|
ISO 527-2/1A |
|
Tensile Stress (Break)
|
|
|
psi
|
ISO 527-2/1A |
|
Tensile Strain (Break)
|
|
|
%
|
ISO 527-2/1A |
|
Flexural Modulus
|
|
|
psi
|
ISO 178 |
|
Charpy Notched Impact Strength
|
|
|
ft·lb/in²
|
ISO 179/1eA |
|
Charpy Unnotched Impact Strength
|
|
|
ft·lb/in²
|
ISO 179/1eU |
|
Notched Izod Impact Strength
|
|
|
ft·lb/in²
|
ISO 180/1A |
|
Heat Deflection Temperature (264 psi, Unannealed)
|
|
--
|
°F
|
ISO 75-2/Af |
|
Melting Temperature (DSC)
|
|
--
|
°F
|
ISO 3146 |
|
CLTE - Transverse (73 to 185°F)
|
|
--
|
in/in/°F
|
ISO 11359-2 |
|
Surface Resistivity
|
|
|
ohm
|
IEC 60093 |
|
Volume Resistivity
|
|
|
ohm·cm
|
IEC 60093 |
|
Relative Permittivity
|
|
|
|
IEC 60250 |
|
Dissipation Factor
|
|
|
|
IEC 60250 |
|
Comparative Tracking Index (Solution A)
|
|
|
V
|
IEC 60112 |
|
Electric Strength
|
|
|
V/mil
|
IEC 60243-1 |
|
Flame Rating - UL (0.0630 in)
|
|
--
|
|
UL 94 |
|
|
The value listed as Melting Temperature (DSC), ISO 3146, was tested in accordance with ISO 11357.
Molding Shrinkage, Rhodia Method, Isotropy: 0.54
Molding Shrinkage, Rhodia Method, Normal/Perpendicular: 1.2%
Molding Shrinkage, Rhodia Method, Parallel: 0.65%
|
|
|
Product names can be difficult to match. You may have searched any one of these terms to find this product: TECHNYL® A 218 MT15 V25 BLACK 21 N, TECHNYL A 218 MT15 V25 BLACK 21 N, TECHNYL® A , TECHNYL A, TECHNYLA218MT15V25BLACK21N, TECHNYLA, A 218 MT 15 V 25 BLACK 21 N, A218 MT15 V25 BLACK 21 N, A218, 218 MT 15 V 25 BLACK 21 N, A218MT15V25BLACK21N, 218 MT15 V25 BLACK 21 N, 218MT, MT15, 15V, V25, 25BLACK, BLACK21, 21N, 218MT15V25BLACK21N, Polyamide 66, Nylon 66, Polyamide, Nylon, pa66, Rhodia, Polyamide66, Nylon66, MT218, 218A
|
|
|
Generic Name may also be described by the following terms: PA66.
|
|
|
Generic Name may also be described by the following terms: PA66.
|
|
|
Features may also be described by the following terms: Heat Stabilized, Heat-ageing Stabilized, Heat Ageing Stabilized, Heat-aging Stabilized, Heat Aging Stabilized, Low Warpage, Low Warp.
|
|
|
Uses may also be described by the following terms: Automotive Applications, Automotive Sector.
|
|
|
Product names can be difficult to match. You may have searched any one of these terms to find this product: TECHNYL® A 218 MT15 V25 BLACK 21 N, TECHNYL A 218 MT15 V25 BLACK 21 N, TECHNYL® A , TECHNYL A, TECHNYLA218MT15V25BLACK21N, TECHNYLA, A 218 MT 15 V 25 BLACK 21 N, A218 MT15 V25 BLACK 21 N, A218, 218 MT 15 V 25 BLACK 21 N, A218MT15V25BLACK21N, 218 MT15 V25 BLACK 21 N, 218MT, MT15, 15V, V25, 25BLACK, BLACK21, 21N, 218MT15V25BLACK21N, Polyamide 66, Nylon 66, Polyamide, Nylon, pa66, Rhodia, Polyamide66, Nylon66, MT218, 218A
|