Specific Gravity
|
|
|
|
|
--
|
|
|
ASTM D792 |
|
--
|
|
g/cm³
|
ISO 1183, ASTM D792 |
|
Specific Volume
|
|
in³/lb
|
ASTM D792 |
|
Melt Mass-Flow Rate (MFR)
|
|
|
|
|
250°C/2.16 kg
|
|
g/10 min
|
ASTM D1238, ISO 1133 |
|
250°C/5.0 kg
|
|
g/10 min
|
ASTM D1238, ISO 1133 |
|
265°C/2.16 kg
|
|
g/10 min
|
ASTM D1238 |
|
266°C/5.0 kg
|
|
g/10 min
|
ASTM D1238 |
|
Melt Volume-Flow Rate (MVR)
|
|
|
ISO 1133 |
|
250°C/2.16 kg
|
|
in³/10min
|
|
|
250°C/5.0 kg
|
|
in³/10min
|
|
|
265°C/2.16 kg
|
|
in³/10min
|
|
|
265°C/5.0 kg
|
|
in³/10min
|
|
|
Molding Shrinkage - Flow (0.126 in)
|
|
in/in
|
Internal Method |
|
Water Absorption
|
|
|
ISO 62 |
|
Saturation, 73°F
|
|
%
|
|
|
Equilibrium, 73°F, 50% RH
|
|
%
|
|
|
Tensile Modulus
|
|
|
|
|
-- 2
|
|
psi
|
ASTM D638 |
|
-- 3
|
|
psi
|
Internal Method |
|
-- 4
|
|
psi
|
ASTM D638 |
|
--
|
|
psi
|
ISO 527-2/1 |
|
Tensile Strength
|
|
|
|
|
Yield 5
|
|
psi
|
ASTM D638 |
|
Yield 6
|
|
psi
|
Internal Method |
|
Yield 7
|
|
psi
|
ASTM D638 |
|
Yield
|
|
psi
|
ISO 527-2/5 |
|
Yield
|
|
psi
|
ISO 527-2/50 |
|
Break 5
|
|
psi
|
ASTM D638 |
|
Break 6
|
|
psi
|
Internal Method |
|
Break 7
|
|
psi
|
ASTM D638 |
|
Break
|
|
psi
|
ISO 527-2/5, ISO 527-2/50 |
|
Tensile Elongation
|
|
|
|
|
Yield 5
|
|
%
|
ASTM D638 |
|
Yield 6
|
|
%
|
Internal Method |
|
Yield 7
|
|
%
|
ASTM D638 |
|
Yield
|
|
%
|
ISO 527-2/5 |
|
Yield
|
|
%
|
ISO 527-2/50 |
|
Break 5
|
|
%
|
ASTM D638 |
|
Break 6
|
|
%
|
Internal Method |
|
Break 7
|
|
%
|
ASTM D638 |
|
Break
|
|
%
|
ISO 527-2/5 |
|
Break
|
|
%
|
ISO 527-2/50 |
|
Flexural Modulus
|
|
|
|
|
1.97 in Span 8
|
|
psi
|
ASTM D790 |
|
-- 9
|
|
psi
|
ISO 178 |
|
Flexural Strength
|
|
|
|
|
-- 9, 10
|
|
psi
|
ISO 178 |
|
Yield, 1.97 in Span 8
|
|
psi
|
ASTM D790 |
|
Break, 1.97 in Span 8
|
|
psi
|
ASTM D790 |
|
Charpy Notched Impact Strength 11
|
|
|
ISO 179/1eA |
|
-22°F
|
|
ft·lb/in²
|
|
|
73°F
|
|
ft·lb/in²
|
|
|
Notched Izod Impact
|
|
|
|
|
-40°F
|
|
ft·lb/in
|
ASTM D256 |
|
-22°F
|
|
ft·lb/in
|
ASTM D256 |
|
-4°F
|
|
ft·lb/in
|
ASTM D256 |
|
14°F
|
|
ft·lb/in
|
ASTM D256 |
|
32°F
|
|
ft·lb/in
|
ASTM D256 |
|
73°F
|
|
ft·lb/in
|
ASTM D256 |
|
-40°F 12
|
|
ft·lb/in²
|
ISO 180/1A |
|
-22°F 12
|
|
ft·lb/in²
|
ISO 180/1A |
|
-4°F 12
|
|
ft·lb/in²
|
ISO 180/1A |
|
14°F 12
|
|
ft·lb/in²
|
ISO 180/1A |
|
32°F 12
|
|
ft·lb/in²
|
ISO 180/1A |
|
73°F 12
|
|
ft·lb/in²
|
ISO 180/1A |
|
Instrumented Dart Impact
|
|
|
ASTM D3763 |
|
-40°F, Energy at Peak Load
|
|
in·lb
|
|
|
-40°F, Total Energy
|
|
in·lb
|
|
|
-22°F, Energy at Peak Load
|
|
in·lb
|
|
|
-22°F, Total Energy
|
|
in·lb
|
|
|
-4°F, Energy at Peak Load
|
|
in·lb
|
|
|
-4°F, Total Energy
|
|
in·lb
|
|
|
73°F, Energy at Peak Load
|
|
in·lb
|
|
|
73°F, Total Energy
|
|
in·lb
|
|
|
Deflection Temperature Under Load
|
|
|
|
|
66 psi, Unannealed, 0.126 in
|
|
°F
|
ASTM D648 |
|
66 psi, Unannealed, 0.252 in
|
|
°F
|
ASTM D648 |
|
66 psi, Unannealed, 2.52 in Span 13
|
|
°F
|
ISO 75-2/Bf |
|
264 psi, Unannealed, 0.126 in
|
|
°F
|
ASTM D648 |
|
264 psi, Unannealed, 0.252 in
|
|
°F
|
ASTM D648 |
|
264 psi, Unannealed, 2.52 in Span 13
|
|
°F
|
ISO 75-2/Af |
|
Vicat Softening Temperature
|
|
|
|
|
--
|
|
°F
|
ASTM D1525 14, ISO 306/B50 14 |
|
--
|
|
°F
|
ISO 306/B120 |
|
CLTE
|
|
|
|
|
Flow: -40 to 203°F
|
|
in/in/°F
|
ASTM E831 |
|
Flow: -22 to 176°F
|
|
in/in/°F
|
ISO 11359-2 |
|
Transverse: -40 to 203°F
|
|
in/in/°F
|
ASTM E831 |
|
Transverse: -22 to 176°F
|
|
in/in/°F
|
ISO 11359-2 |
|
This supplier and product may also be known by these terms: GE Plastics, LNP Engineering Plastics
Product names can be difficult to match. You may have searched any one of these terms to find this product: XENOY* 5720U Resin, XENOY 5720U Resin, XENOY* , XENOY, XENOY5720UResin, 5720 U Resin, 5720U Resin, 5720U, UResin, 5720UResin, Polycarbonate + PBT, Polycarbonate PBT, Polycarbonate : PBT, Polycarbonate / PBT, Polycarbonate - PBT, Polycarbonate _ PBT, Polycarbonate PBT, PC+PBT, PCPBT, PC:PBT, PC/PBT, PC-PBT, PC_PBT, PC PBT, Polycarbonate, PC, SABIC IP Asia, PolycarbonatePBT, Polycarbonate_PBT, U5720
|
|
Features may also be described by the following terms: Good Chemical Resistance, Chemical Resistant, Low Temperatuer Impact Resistance, Low Temp Impact Resistance.
|