CYCOLOY* CE8510 Resin

Acrylonitrile Butadiene Styrene + PC

Supplied by SABIC Innovative Plastics Europe

The technical datasheet with complete property values for CYCOLOY* CE8510 Resin is available to members of the Prospector Plastics Database.
Register to view full datasheet.
Register to View Full Datasheet
Product Description
Extrusion grade PC/ABS. Low viscosity, high impact and ductility.
General  
Material Status 
  • Commercial: Active
Availability 
  • Europe
Features 
  • Ductile
  • High Impact Resistance
  • Low Viscosity
RoHS Compliance 
Processing Method 
  • Film Extrusion
Physical
Nominal Value
Unit
Test Method
Specific Gravity
      
--
 
 ASTM D792
--
g/cm³
 ISO 1183
Melt Mass-Flow Rate (MFR) (260°C/5.0 kg)
g/10 min
 ASTM D1238
Melt Volume-Flow Rate (MVR) (265°C/5.0 kg)
in³/10min
 ISO 1133
Molding Shrinkage
     Internal Method
Flow: 0.126 in
in/in
  
Across Flow: 0.126 in
in/in
  
Water Absorption
     ISO 62
Saturation, 73°F
%
  
Equilibrium, 73°F, 50% RH
%
  
Mechanical
Nominal Value
Unit
Test Method
Tensile Modulus
      
-- 2
psi
 ASTM D638
--
psi
 ISO 527-2/1
Tensile Strength
      
Yield 3
psi
 ASTM D638
Yield
psi
 ISO 527-2/50
Break 3
psi
 ASTM D638
Break
psi
 ISO 527-2/50
Tensile Elongation
      
Yield 3
%
 ASTM D638
Yield
%
 ISO 527-2/50
Break 3
%
 ASTM D638
Break
%
 ISO 527-2/50
Flexural Modulus
      
1.97 in Span 4
psi
 ASTM D790
-- 5
psi
 ISO 178
Flexural Strength
      
-- 5, 6
psi
 ISO 178
Yield, 1.97 in Span 4
psi
 ASTM D790
Impact
Nominal Value
Unit
Test Method
Charpy Notched Impact Strength 7
     ISO 179/1eA
-22°F
ft·lb/in²
  
73°F
ft·lb/in²
  
Notched Izod Impact
      
-22°F
ft·lb/in
 ASTM D256
73°F
ft·lb/in
 ASTM D256
-22°F 8
ft·lb/in²
 ISO 180/1A
73°F 8
ft·lb/in²
 ISO 180/1A
Instrumented Dart Impact (73°F, Total Energy)
in·lb
 ASTM D3763
Thermal
Nominal Value
Unit
Test Method
Deflection Temperature Under Load
      
66 psi, Unannealed, 0.126 in
°F
 ASTM D648
264 psi, Unannealed, 0.126 in
°F
 ASTM D648
264 psi, Unannealed, 2.52 in Span 9
°F
 ISO 75-2/Af
Vicat Softening Temperature
      
--
°F
 ASTM D1525 10, ISO 306/B50 10
--
°F
 ISO 306/B120
Ball Pressure Test (167°F)
 
 IEC 60695-10-2
CLTE
     ASTM E831, ISO 11359-2
Flow: -40 to 104°F
in/in/°F
  
Transverse: -40 to 104°F
in/in/°F
  
Related Terminology
This supplier and product may also be known by these terms: GE Plastics Europe, LNP Engineering Plastics, GE Polymerland Europe, GE Polymerland, GE Plastics, Cycloy

Product names can be difficult to match. You may have searched any one of these terms to find this product: CYCOLOY* CE8510 Resin, CYCOLOY CE8510 Resin, CYCOLOY* , CYCOLOY, CYCOLOYCE8510Resin, CE 8510 Resin, CE8510 Resin, CE8510, 8510Resin, CE8510Resin, Acrylonitrile Butadiene Styrene + PC, Acrylonitrile Butadiene Styrene PC, Acrylonitrile Butadiene Styrene : PC, Acrylonitrile Butadiene Styrene / PC, Acrylonitrile Butadiene Styrene - PC, Acrylonitrile Butadiene Styrene _ PC, Acrylonitrile Butadiene Styrene PC, ABS+PC, ABSPC, ABS:PC, ABS/PC, ABS-PC, ABS_PC, ABS PC, Acrylonitrile Butadiene Styrene, ABS, SABIC IP Euro, AcrylonitrileButadieneStyrenePC, AcrylonitrileButadieneStyrene, AcrylonitrileButadieneStyrene_PC, 8510CE
Features
Features may also be described by the following terms: High Impact Resistance, Low Viscosity.
Extrusion
Nominal Value
Unit
 
Drying Temperature
°F
  
Drying Time
hr
  
Suggested Max Moisture
%
  
Cylinder Zone 1 Temp.
°F
  
Cylinder Zone 3 Temp.
°F
  
Cylinder Zone 5 Temp.
°F
  
Die Temperature
°F
  
Extrusion Notes
Drying Time (Cumulative): 6 - 8 hrs
Roll Temperature: 200 - 250 °C
Notes
1Typical properties: these are not to be construed as specifications.
20.20 in/min
3Type I, 2.0 in/min
40.051 in/min
50.079 in/min
6Yield
780*10*3 sp=62mm
880*10*3
980*10*4 mm
10Rate B (120°C/h), Loading 2 (50 N)
 
IDES
Copyright © 2012 IDES
The information presented on this datasheet was acquired by IDES from the producer of the material. IDES makes substantial efforts to assure the accuracy of this data. However, IDES assumes no responsibility for the data values and strongly encourages that upon final material selection, data points are validated with the material supplier.