PRE-ELEC CP 1319 Premix OY Ethylene Vinyl Acetate Copolymer

Product Description

PRE-ELEC CP 1319 is a conductive thermoplastic compound based on EVA. Conductivity is achieved by using special conductive carbon black. In addition to a low electrical resistivity PRE-ELEC CP 1319 has excellent mechanical properties and is suitable for film blowing. It is also suitable for coextrusion applications.

Typical applications include blown film for the production of bags for electronic components and other products that are sensitive to static electricity.

General

Material Status

Commercial: Active

Availability

Asia Pacific

Europe

North America

South America

Additive

Carbon Black

Features

Electrically Conductive

Uses

Bags

Electrical/Electronic Applications

Film

Appearance

Black

Forms

Granules

Processing Method

Blown Film

Coextrusion

Physical	Nominal Value	Unit	Test Method
Specific Gravity
--			ASTM D792
--		g/cm³	ISO 1183
Melt Mass-Flow Rate (MFR) (190°C/5.0 kg)		g/10 min	ISO 1133
Films	Nominal Value	Unit	Test Method
Tensile Strength
MD: Yield, 16 mil		psi	ASTM D882
TD: Yield, 16 mil		psi	ASTM D882
MD: Yield, 16 mil		psi	ISO 527-3
TD: Yield, 16 mil		psi	ISO 527-3
MD: Break, 16 mil		psi	ASTM D882
TD: Break, 16 mil		psi	ASTM D882
MD: 16 mil		psi	ISO 527-3
TD: 16 mil		psi	ISO 527-3
Tensile Elongation - MD (Break, 16 mil)		%	ISO 527-3
Additional Information
Elongation at Yield, ISO 527, 400µm, MD: 70% Elongation at Yield, ISO 527, 400µm, TD: 60%
Related Terminology
Product names can be difficult to match. You may have searched any one of these terms to find this product: PRE-ELEC CP 1319, PREELEC CP 1319, PRE-ELEC , PREELEC, PRE:ELEC, PRE/ELEC, PRE+ELEC, PRE_ELEC, PRE ELEC, PREELECCP1319, CP 1319, CP1319, Ethylene Vinyl Acetate Copolymer, EVA, Polyethylene, PE, Premix OY, EthyleneVinylAcetateCopolymer, 1319CP
Features
Features may also be described by the following terms: Electrically Conductive, Conducts Electricity, Conductive.
Uses
Uses may also be described by the following terms: Electrical Applications, Electronic Applications, Electrical/Electronic Applications, Electrical Sector.

Extrusion	Nominal Value	Unit
Drying Temperature		°F
Drying Time		hr
Extrusion Notes
Temperature Settings: 155 to 200°C Blowing Ratio: >1.8 Screen Pack: as coarse as possible

Notes

¹Typical properties: these are not to be construed as specifications.

PRE-ELEC CP 1319

Ethylene Vinyl Acetate Copolymer

Supplied by PREMIX OY