Specific Gravity
|
|
|
|
|
--
|
|
|
ASTM D792 |
|
--
|
|
g/cm³
|
ISO 1183 |
|
Molding Shrinkage
|
|
|
|
|
Flow
|
|
in/in
|
ASTM D955 |
|
Across Flow
|
|
in/in
|
ASTM D955 |
|
Across Flow
|
|
%
|
ISO 294-4 |
|
Flow
|
|
%
|
ISO 294-4 |
|
Water Absorption (73°F, 24 hr)
|
|
%
|
ASTM D570, ISO 62 |
|
Tensile Modulus
|
|
|
|
|
--
|
|
psi
|
ASTM D638 |
|
--
|
|
psi
|
ISO 527-2/1 |
|
Tensile Strength
|
|
|
|
|
Break
|
|
psi
|
ASTM D638 |
|
Break
|
|
psi
|
ISO 527-2/5 |
|
Tensile Elongation
|
|
|
|
|
Break
|
|
%
|
ASTM D638 |
|
Break
|
|
%
|
ISO 527-2/5 |
|
Flexural Modulus
|
|
|
|
|
--
|
|
psi
|
ASTM D790 |
|
-- 2
|
|
psi
|
ISO 178 |
|
Flexural Strength
|
|
|
|
|
--
|
|
psi
|
ASTM D790 |
|
-- 2
|
|
psi
|
ISO 178 |
|
Compressive Strength
|
|
psi
|
ASTM D695 |
|
Charpy Notched Impact Strength
|
|
ft·lb/in²
|
ISO 179 |
|
Charpy Unnotched Impact Strength
|
|
ft·lb/in²
|
ISO 179 |
|
Notched Izod Impact
|
|
|
ASTM D256 |
|
0.126 in
|
|
ft·lb/in
|
|
|
0.252 in
|
|
ft·lb/in
|
|
|
Rockwell Hardness (M-Scale)
|
|
|
ASTM D785 |
|
Deflection Temperature Under Load
|
|
|
|
|
66 psi, Unannealed
|
|
°F
|
ASTM D648 |
|
66 psi, Unannealed
|
|
°F
|
ISO 75-2/B |
|
264 psi, Unannealed
|
|
°F
|
ASTM D648 |
|
264 psi, Unannealed
|
|
°F
|
ISO 75-2/A |
|
Vicat Softening Temperature
|
|
°F
|
ISO 306/B50 |
|
CLTE
|
|
|
|
|
Flow
|
|
in/in/°F
|
ASTM D696 |
|
Flow
|
|
in/in/°F
|
ISO 11359-2 |
|
Transverse
|
|
in/in/°F
|
ASTM D696 |
|
Transverse
|
|
in/in/°F
|
ISO 11359-2 |
|
Surface Resistivity
|
|
ohms
|
IEC 60093 |
|
Volume Resistivity
|
|
|
|
|
--
|
|
ohm·cm
|
ASTM D257 |
|
--
|
|
ohm·cm
|
IEC 60093 |
|
Dielectric Strength
|
|
|
|
|
0.0630 in
|
|
V/mil
|
ASTM D149 |
|
--
|
|
V/mil
|
IEC 60243-1 |
|
Dielectric Constant
|
|
|
|
|
60 Hz
|
|
|
ASTM D150 |
|
1 MHz
|
|
|
ASTM D150 |
|
100 Hz
|
|
|
IEC 60250 |
|
1 MHz
|
|
|
IEC 60250 |
|
Dissipation Factor
|
|
|
|
|
60 Hz
|
|
|
ASTM D150 |
|
1 MHz
|
|
|
ASTM D150, IEC 60250 |
|
100 Hz
|
|
|
IEC 60250 |
|
Arc Resistance
|
|
sec
|
ASTM D495 |
|
Comparative Tracking Index
|
|
V
|
IEC 60112 |
|
Flame Rating - UL
|
|
|
UL 94 |
|
0.0169 in
|
|
|
|
|
0.0315 in
|
|
|
|
|
0.118 in
|
|
|
|
|
RTI Str (0.0579 in)
|
|
°F
|
UL 746 |
|
RTI Imp (0.0579 in)
|
|
°F
|
UL 746 |
|
RTI Elec (0.0579 in)
|
|
°F
|
UL 746 |
|
The value listed as Specific Gravity, ASTM D792, was tested in accordance with JIS K7112.
The values listed as Heat Deflection Temperature, ASTM D648, were tested in accordance with JIS K7207.
Mold Shrinkage, In House Method, Flow, 4 mm: 0.2 to 0.4 %
Mold Shrinkage, In House Method, Across Flow, 4 mm: 0.4 to 0.6 %
|
|
Product names can be difficult to match. You may have searched any one of these terms to find this product: Panlite® G-3415R, Panlite G3415R, Panlite® , Panlite, PanliteG3415R, G 3415 R, G-3415R, G3415R, G:3415R, G/3415R, G+3415R, G_3415R, G 3415R, G3415, 3415R, Polycarbonate, PC, Teijin, 3415G
|
|
Features may also be described by the following terms: High Rigidity, Good Mold Release, Easy Release, Good Demolding.
|
|
Uses may also be described by the following terms: Machine Parts, Mechanical Parts, Machine/Mechanical Parts, Housings, Housing, Power Tools, Tools.
|