AQUAMID 66G25V0P 1001 Aquafil Polyamide 66 (Glass Fiber Reinforcement, 25%)

General
Material Status	Commercial: Active
Availability	Europe
Filler / Reinforcement	Glass Fiber Reinforcement, 25% Filler by Weight
Features	Flame Retardant
Forms	Pellets
Processing Method	Injection Molding

Physical	Nominal Value	Unit	Test Method
Density		g/cm³	ISO 1183
Molding Shrinkage (73°F)		%	ISO 294-4
Water Absorption (73°F, 24 hr)		%	ISO 62
Mechanical	Nominal Value	Unit	Test Method
Tensile Modulus (73°F)		psi	ISO 527-2/1
Tensile Stress (Break, 73°F)		psi	ISO 527-2/5
Tensile Strain (Break, 73°F)		%	ISO 527-2/5
Flexural Modulus² (73°F)		psi	ISO 178
Impact	Nominal Value	Unit	Test Method
Notched Izod Impact Strength (73°F)		ft·lb/in²	ISO 180/1A
Thermal	Nominal Value	Unit	Test Method
Heat Deflection Temperature (66 psi, Unannealed)		°F	ISO 75-2/B
Vicat Softening Temperature		°F	ISO 306/B50
Melting Temperature (DSC)		°F	ISO 3146
Electrical	Nominal Value	Unit	Test Method
Surface Resistivity		ohms	IEC 60093
Volume Resistivity		ohm·cm	IEC 60093
Comparative Tracking Index (Solution A)		V	IEC 60112
Flammability	Nominal Value	Unit	Test Method
Flame Rating - UL (0.0315 in)			UL 94
Glow Wire Ignition Temperature (0.0787 in)		°F	IEC 60695-2-13
Additional Information
Mold Shrinkage, ISO 2577, 23°C: 0.3 to 0.6 % Melting Point, DSC: 260 ± 2 °C
Related Terminology
Product names can be difficult to match. You may have searched any one of these terms to find this product: AQUAMID 66G25V0P 1001, AQUAMID , AQUAMID66G25V0P1001, 66 G 25 V 0 P 1001, 66G25V0P 1001, 66G, G25, 25V, V0, 0P, P1001, 66G25V0P1001, Polyamide 66, Nylon 66, Polyamide, Nylon, pa66, Aquafil, Polyamide66, Nylon66, G66
Generic Name
Generic Name may also be described by the following terms: PA66.

Notes

¹Typical properties: these are not to be construed as specifications.

²0.079 in/min

AQUAMID 66G25V0P 1001