Density
|
|
g/cm³
|
ISO 1183 |
|
Melt Mass-Flow Rate (MFR) (190°C/2.16 kg)
|
|
g/10 min
|
ISO 1133 |
|
Melt Volume-Flow Rate (MVR) (190°C/2.16 kg)
|
|
in³/10min
|
ISO 1133 |
|
Molding Shrinkage - Flow (0.0787 in)
|
|
%
|
ISO 294-4 |
|
Water Absorption
|
|
|
ISO 62 |
|
Saturation, 73°F
|
|
%
|
|
|
Equilibrium, 73°F, 50% RH
|
|
%
|
|
|
Tensile Modulus
|
|
psi
|
ISO 527-2/1 |
|
Tensile Stress (Yield)
|
|
psi
|
ISO 527-2/50 |
|
Tensile Strain
|
|
|
ISO 527-2/50 |
|
Yield
|
|
%
|
|
|
Break
|
|
%
|
|
|
Flexural Modulus 2
|
|
psi
|
ISO 178 |
|
Flexural Strength 2
|
|
psi
|
ISO 178 |
|
Charpy Notched Impact Strength
|
|
ft·lb/in²
|
ISO 179/1eA |
|
Charpy Unnotched Impact Strength
|
|
|
ISO 179/1eU |
|
Notched Izod Impact Strength
|
|
ft·lb/in²
|
ISO 180 |
|
Ball Indentation Hardness (H 358/30)
|
|
psi
|
ISO 2039-1 |
|
Heat Deflection Temperature (264 psi, Unannealed)
|
|
°F
|
ISO 75-2/A |
|
Vicat Softening Temperature
|
|
°F
|
ISO 306/B |
|
Melting Temperature
|
|
°F
|
ISO 11357-3 |
|
CLTE - Flow (73 to 131°F)
|
|
in/in/°F
|
ISO 11359-2 |
|
Limit of Temperature - a few hours operation
|
|
°F
|
|
|
Surface Resistivity
|
|
ohms
|
IEC 60093 |
|
Volume Resistivity
|
|
ohm·cm
|
IEC 60093 |
|
Dielectric Constant (1 Hz)
|
|
|
IEC 60250 |
|
Dissipation Factor (1 Hz)
|
|
|
IEC 60250 |
|
Comparative Tracking Index (Solution A)
|
|
V
|
IEC 60112 |
|
Electric Strength (0.0787 in)
|
|
V/mil
|
IEC 60243-1 |
|
Flame Rating - UL (0.126 in)
|
|
|
UL 94 |
|
Burning Rate
|
|
in/min
|
FMVSS 302 |
|
ISO Type
|
|
|
ISO 1874 |
|
Product names can be difficult to match. You may have searched any one of these terms to find this product: Tarnoform® 300 CI4, Tarnoform 300 CI4, Tarnoform® , Tarnoform, Tarnoform300CI4, 300 CI 4, 300 CI4, 300CI, CI4, 300CI4, Acetal Copolymer, Acetal Copolymer, Acetal (POM) Copolymer, Acetal POM Copolymer, Acetal, pom, Zaktady Azotowe, AcetalPOMCopolymer, CI300
|
|
Features may also be described by the following terms: Good Impact Resistance, Low Temperatuer Impact Resistance, Low Temp Impact Resistance.
|