INEOS LLDPE LL6608LJ Ineos Polyolefins Polyethylene, Linear Low Density

Product Description

LL6608LJ has been developed for the production of mailing film, carrier, bread and produce bags.

LL6608LJ is a linear low density polyethylene copolymer containing hexene-1 as the co-monomer. It offers the following properties:

Optimum balance between stiffness and film strength

Good optical properties

Good bubble stability

Excellent sealability and hot-tack strength

LL6608LJ offers high slip film with easy opening properties when used pure in the thickness range 30 to 70 µm. Addition of other polymers, masterbatch and pigments, or the use of other thicknesses may alter film slip and antiblock performance.

If corona treatment is necessary, the level should normally be in the range 38-48 mN/m.
We recommend that you consult your Innovene technical representative for further advice on the
use of LL6608LJ.

General

Material Status

Commercial: Active

Availability

Europe

Additive

Antiblock (600 ppm)

Antioxidant

Slip (1200 ppm)

Features

Antiblocking

Antioxidant

Copolymer

Good Heat Seal

Good Stiffness

Good Strength

Hexene Comonomer

High Slip

Opticals

Uses

Bags

Film

RoHS Compliance

Forms

Pellets

Processing Method

Film Extrusion

Physical	Nominal Value	Unit	Test Method
Density		g/cm³	ISO 1183/D
Melt Mass-Flow Rate (MFR) (190°C/2.16 kg)		g/10 min	ISO 1133
Mechanical	Nominal Value	Unit	Test Method
Coefficient of Friction (Blown Film)			ASTM D1894
Films	Nominal Value	Unit	Test Method
Film Thickness - Tested		mil
Tensile Modulus - 1% Secant (1.5 mil, Blown Film)		psi	ISO 1184
Tensile Stress			ISO 527-3
MD: Yield, 1.5 mil, Blown Film		psi
TD: Yield, 1.5 mil, Blown Film		psi
MD: 1.5 mil, Blown Film		psi
TD: 1.5 mil, Blown Film		psi
Tensile Elongation			ISO 1184
MD: Break, 1.5 mil, Blown Film		%
TD: Break, 1.5 mil, Blown Film		%
Dart Drop Impact (1.5 mil, Blown Film)		g	ASTM D1709A
Elmendorf Tear Strength²			ASTM D1922
MD: 1.5 mil		lbf/in
TD: 1.5 mil		lbf/in
Thermal	Nominal Value	Unit	Test Method
Vicat Softening Temperature		°F	ISO 306/A50
Optical	Nominal Value	Unit	Test Method
Gloss (45°, 1.50 mil)			ASTM D2457
Haze		%	ASTM D1003
Additional Information
Film properties taken from 38 µm film, 2:1 blow up ratio, 230°C melt temperature.
Related Terminology
Product names can be difficult to match. You may have searched any one of these terms to find this product: INEOS LLDPE LL6608LJ, INEOS LLDPE , INEOSLLDPELL6608LJ, INEOSLLDPE, LLDPELL 6608 LJ, LLDPELL6608LJ, LLDPELL6608, LLDPE, LL 6608 LJ, LL6608LJ, LL6608, 6608LJ, Polyethylene, Linear Low Density, Polyethylene Linear Low Density, Polyethylene, PE, Ineos Polyolefins, PolyethyleneLinearLowDensity, 6608LL, 6608LLDPELL
Features
Features may also be described by the following terms: Good Strength, Good Stiffness, High Slip, Hexene Comonomer, Antiblocking, Unspecified Antiblock, Good Heat Seal.

Extrusion	Nominal Value	Unit
Melt Temperature		°F

Notes

¹Typical properties: these are not to be construed as specifications.

²Blown Film

INEOS LLDPE LL6608LJ

Linear Low Density Polyethylene

Supplied by INEOS Olefins & Polymers Europe