INEOS LLDPE LL0209KJ Ineos Polyolefins Polyethylene, Linear Low Density

Product Description

LL0209KJ are suitable for general purpose films, neat or in blends with LDPE and other ethylene polymers. Lean blend applications include sacks of all types, FFS and agricultural film.

Benefits and Features
LL0209KJ is a linear low density polyethylene copolymers containing butene-1 (C4) as the comonomer. In lean blends, it offers the following advantages compared to LDPE neat:

Greater drawdown

Improved hot-tack and lower seal shrinkage

Better tear resistance

Higher tensile stress and elongation at break

LL0209KJ offers high slip film with easy opening properties when used pure in the thickness range 35 - 100 µm. Addition of other polymers, masterbatches and pigments, or use of other thicknesses may alter film slip and antiblock performance.

If corona treatment is necessary, the level should normally be in the range 38-48 mN/m. We recommend that you consult your INEOS technical representative for further advice on the use of LL0209KJ.

General

Material Status

Commercial: Active

Availability

Europe

Additive

Antiblock (1430 ppm)

Antioxidant

Slip (1180 ppm)

Features

Antiblocking

Antioxidant

Butene Comonomer

Good Drawdown

Good Tear Strength

High Elongation

High Slip

Uses

Blending

Film

RoHS Compliance

Forms

Pellets

Processing Method

Blown Film

Physical	Nominal Value	Unit	Test Method
Density		g/cm³	ISO 1183/D
Melt Mass-Flow Rate (MFR) (190°C/2.16 kg)		g/10 min	ISO 1133
Mechanical	Nominal Value	Unit	Test Method
Coefficient of Friction (Blown Film)			ASTM D1894
Films	Nominal Value	Unit	Test Method
Film Thickness - Tested		mil
Tensile Modulus			ISO 527-3
1% Secant, MD: 1.5 mil, Blown Film		psi
1% Secant, TD: 1.5 mil, Blown Film		psi
Tensile Stress			ISO 527-3
MD: Yield, 1.5 mil, Blown Film		psi
TD: Yield, 1.5 mil, Blown Film		psi
MD: 1.5 mil, Blown Film		psi
TD: 1.5 mil, Blown Film		psi
Tensile Elongation			ISO 527-3
MD: Break, 1.5 mil, Blown Film		%
TD: Break, 1.5 mil, Blown Film		%
Dart Drop Impact (1.5 mil, Blown Film)		g	ASTM D1709A
Elmendorf Tear Strength²			ASTM D1922
MD: 1.5 mil		lbf/in
TD: 1.5 mil		lbf/in
Thermal	Nominal Value	Unit	Test Method
Vicat Softening Temperature		°F	ISO 306/A50
Optical	Nominal Value	Unit	Test Method
Gloss (45°, 1.50 mil, Blown Film)			ASTM D2457
Haze (1.50 mil, Blown Film)		%	ASTM D1003
Additional Information
Film properties taken from 38 µm film, 2.5:1 blow up ratio, 225°C melt temperature.
Related Terminology
Product names can be difficult to match. You may have searched any one of these terms to find this product: INEOS LLDPE LL0209KJ, INEOS LLDPE , INEOSLLDPELL0209KJ, INEOSLLDPE, LLDPELL 0209 KJ, LLDPELL0209KJ, LLDPELL0209, LLDPE, LL 0209 KJ, LL0209KJ, LL0209, 0209KJ, Polyethylene, Linear Low Density, Polyethylene Linear Low Density, Polyethylene, PE, Ineos Polyolefins, PolyethyleneLinearLowDensity, 0209LL, 0209LLDPELL
Features
Features may also be described by the following terms: High Elongation, Antiblocking, Unspecified Antiblock, Butene Comonomer, Good Drawdown, Good draw down, High Slip, Good Tear Strength.

Extrusion	Nominal Value	Unit
Melt Temperature		°F

Notes

¹Typical properties: these are not to be construed as specifications.

²Blown Film

INEOS LLDPE LL0209KJ

Linear Low Density Polyethylene

Supplied by INEOS Olefins & Polymers Europe