Samsung Total E210F

Ethylene Vinyl Acetate Copolymer

Supplied by SAMSUNG TOTAL PETROCHEMICALS Co., Ltd.

The technical datasheet with complete property values for Samsung Total E210F is available to members of the Prospector Plastics Database.
Register to view full datasheet.
Register to View Full Datasheet
Product Description
SAMSUNG TOTAL TOTAL E210F is a EVA (ethylene-vinylacetate copolymer) resin for crosslinked foam applications including mid-sole and in-sole of athletic shoes. This grade is designed to be processed in conventional kneading and rolling equipment for mixing and dispersing crosslinking agent and foaming agent.
General  
Material Status 
  • Commercial: Active
Availability 
  • Asia Pacific
Features 
  • Copolymer
  • Crosslinkable
  • Dispersible
  • Good Processability
  • Good Tear Strength
  • Low Compression Set
Uses 
  • Compounding
  • Foam
  • Footwear
Forms 
  • Pellets
Processing Method 
  • Compounding
  • Compression Molding
  
Physical
Nominal Value
Unit
Test Method
Density
g/cm³
 ASTM D1505
Melt Mass-Flow Rate (MFR) (190°C/2.16 kg)
g/10 min
 ASTM D1238
Environmental Stress-Cracking Resistance (122°F, F10)
hr
 ASTM D1693
Mechanical
Nominal Value
Unit
Test Method
Tensile Strength (Break)
psi
 ASTM D638
Tensile Elongation (Break)
%
 ASTM D638
Apparent Bending Modulus
psi
 ASTM D747
Hardness
Nominal Value
Unit
Test Method
Durometer Hardness
     ASTM D2240
Shore A
 
  
Shore D
 
  
Thermal
Nominal Value
Unit
Test Method
Brittleness Temperature
°F
 ASTM D746
Vicat Softening Temperature
°F
 ASTM D1525 2
Melting Temperature
°F
  
Additional Information
Kneader Temperature: 95 to 105 °C
Foaming Temperature: 155 °C
Foaming Pressure: 150 kg/cm³
Curing Time: 40 min
VA Content, SAMSUNG TOTAL: 21 kg force/cm²
Related Terminology
Product names can be difficult to match. You may have searched any one of these terms to find this product: Samsung Total E210F, Samsung Total , SamsungTotalE210F, SamsungTotal, TotalE 210 F, TotalE210F, TotalE210, Total, E 210 F, E210F, E210, 210F, Ethylene Vinyl Acetate Copolymer, EVA, Polyethylene, PE, EthyleneVinylAcetateCopolymer, 210E, 210TotalE
Features
Features may also be described by the following terms: Good Processability, Easy Processing, Good Tear Strength, Low Compression Set.
Uses
Uses may also be described by the following terms: Compounding, Compounds.
Notes
1Typical properties: these are not to be construed as specifications.
2Loading 1 (10 N)
 
IDES
Copyright © 2012 IDES
The information presented on this datasheet was acquired by IDES from the producer of the material. IDES makes substantial efforts to assure the accuracy of this data. However, IDES assumes no responsibility for the data values and strongly encourages that upon final material selection, data points are validated with the material supplier.