Shincor LIM KEG2002-60 Shincor Sil Silicone

Physical	Nominal Value	Unit	Test Method
Specific Gravity			ASTM D792
Molding Shrinkage - Flow		in/in	ASTM D955
Elastomers	Nominal Value	Unit	Test Method
Tensile Stress (100% Strain)		psi	ASTM D412
Tensile Strength (Yield)		psi	ASTM D412
Tensile Elongation (Break)		%	ASTM D412
Tear Strength		lbf/in	ASTM D624
Hardness	Nominal Value	Unit	Test Method
Durometer Hardness (Shore A)			ASTM D2240
Thermoset	Nominal Value	Unit	Test Method
Post Cure Time (302°F)		hr
Additional Information
Compression Set, ASTM D395, 22 hr, 302°F, Specimen post-cured 1 hr at 302°F: 34% Compression Set, ASTM D395, 22 hr, 302°F, Specimen post-cured 4 hrs at 392°F: 8% Viscosity, Part A: 700 Pa.s Viscosity, Part B: 700 Pa.s Cure Rate, ODR, 302°F, T10: 28 sec Cure Rate, ODR, 302°F, T90: 40 sec Press Cure, 5 min at 302°F
Related Terminology
Product names can be difficult to match. You may have searched any one of these terms to find this product: Shincor LIM KEG2002-60, Shincor LIM KEG200260, Shincor LIM , ShincorLIMKEG200260, ShincorLIM, KEG 2002, LIMKEG 2002 60, LIMKEG 2002, LIMKEG2002-60, LIMKEG200260, LIMKEG2002:60, LIMKEG2002/60, LIMKEG2002+60, LIMKEG2002_60, LIMKEG2002 60, LIMKEG2002, KEG 2002 60, KEG2002-60, KEG200260, KEG2002:60, KEG2002/60, KEG2002+60, KEG2002_60, KEG2002 60, KEG2002, 200260, Silicone, Shincor Sil, 2002KEG, 2002LIMKEG
Features
Features may also be described by the following terms: Low Viscosity.

Notes

¹Typical properties: these are not to be construed as specifications.

Shincor LIM KEG2002-60