Celstran PA66-GF40-02P11/15 Ticona Polyamide 66 (Long Glass Fiber, 40%)

Product Description

Material code according to ISO 1043-1: PA66

Heat stabilized Nylon 66 reinforced by 40 weight percent long glass
fibers. The pellets are cylindrical and normally as well as the
embedded fibers 10 mm long.

Parts molded of CELSTRAN have outstanding mechanical properties such
as high strength and stiffness combined with high heat deflection.
The notched impact strength is increased at elevated and low
temperatures due to the fiber skeleton built in the parts. The long
fiber reinforcement reduces creep significantly.

The very isotropic shrinkage in the molded parts minimizes the
warpage.

Complex parts can be manufactured with high reproducibility by
injection molding.

Can be used for substituting die cast metal with the advantage of
Weight reduction, no corrosion problems, no post treatment.

General

Material Status

Commercial: Active

Availability

Europe

Filler / Reinforcement

Long Glass Fiber, 40% Filler by Weight

Additive

Heat Stabilizer

Features

Heat Stabilized

High Heat Resistance

High Stiffness

High Strength

Low Warpage

Uses

Metal Replacement

RoHS Compliance

Processing Method

Injection Molding

Sheet Extrusion

Resin ID (ISO 1043)

PA66

Physical	Nominal Value	Unit	Test Method
Density		g/cm³	ISO 1183
Viscosity Number		cm³/g	ISO 307
Mechanical	Nominal Value	Unit	Test Method
Tensile Modulus
--		psi	ISO 527-2/1A/1
176°F		psi	ISO 527-2
Tensile Stress (Break)		psi	ISO 527-2/1A/5
Tensile Strain
Break		%	ISO 527-2/1A/5
Break, 176°F		%	ISO 527-2
Flexural Modulus			ISO 178
73°F		psi
176°F		psi
Flexural Strength			ISO 178
176°F		psi
73°F		psi
Tensile Strength (176°F)		psi	ISO 527-2
Impact	Nominal Value	Unit	Test Method
Charpy Notched Impact Strength			ISO 179/1eA
-22°F		ft·lb/in²
73°F		ft·lb/in²
Charpy Unnotched Impact Strength			ISO 179/1eU
-22°F		ft·lb/in²
73°F		ft·lb/in²
Notched Izod Impact Strength			ISO 180/1A
-22°F		ft·lb/in²
73°F		ft·lb/in²
Thermal	Nominal Value	Unit	Test Method
Heat Deflection Temperature
264 psi, Unannealed		°F	ISO 75-2/A
1160 psi, Unannealed		°F	ISO 75-2/C
Melting Temperature²		°F	ISO 11357-3
Related Terminology
Product names can be difficult to match. You may have searched any one of these terms to find this product: Celstran® PA66-GF40-02P11/15, Celstran PA66GF4002P1115, Celstran® , Celstran, CelstranPA66GF4002P1115, PA 66, PA 66 GF 40 02 P 11 15, PA66-GF40-02P11/15, PA66GF4002P1115, PA66-GF40-02P11:15, PA66-GF40-02P11+15, PA66-GF40-02P11-15, PA66-GF40-02P11_15, PA66-GF40-02P11 15, PA66:GF40:02P11/15, PA66/GF40/02P11/15, PA66+GF40+02P11/15, PA66_GF40_02P11/15, PA66 GF40 02P11/15, PA66, 66GF, GF40, 4002, 02P, P11, 1115, PA66GF4002P11_15, PA66GF4002P11 15, PA66_GF40_02P1115, PA66 GF40 02P1115, Polyamide 66, Nylon 66, Polyamide, Nylon, Ticona, Polyamide66, Nylon66, 66PA
Generic Name
Generic Name may also be described by the following terms: PA66.
Features
Features may also be described by the following terms: High Heat Resistance, High Strength, Low Warpage, Low Warp, High Stiffness, Heat Stabilized, Heat-ageing Stabilized, Heat Ageing Stabilized, Heat-aging Stabilized, Heat Aging Stabilized.

Injection	Nominal Value	Unit
Processing (Melt) Temp		°F
Mold Temperature		°F
Injection Notes
During the processing of CELSTRAN it is important to watch and control melt shear, for excessive shear reduces fiber length and mechanical performance as well. Processing recommendation: Conventional 3 zone screw, screw diameter minimum 40 mm Design flow channels for low melt shear Back pressure and screw rotation to realize a continous plastification performance and thus a homogeneous melt. Apply higher temperature settings than for short fiber compounds

Notes

¹Typical properties: these are not to be construed as specifications.

²10°C/min

Celstran® PA66-GF40-02P11/15

Polyamide 66

Long Glass Fiber, 40%