Hostaform C 13031 K Ticona Acetal (POM) Copolymer (Chalk Filler)

Product Description

Chemical abbreviation according to ISO 1043-1: POM
Molding compound ISO 9988- POM-K, M-GNR, 04-002, K5

POM copolymer

Easy flowing Injection molding type with higher strength, rigidity
and hardness with special chalk modified good chemical resistance
to solvents, fuel and strong alkalis as well as good hydrolysis
resistance high resistance to thermal and oxidative degradation
good wear properties

UL-registration in natural and a thickness more than 1.5 mm as UL 94
HB.

Burning rate ISO 3795 and FMVSS 302 < 100 mm/min for a thickness
more than 1 mm.

Ranges of applications: For unlubricated or once-only-lubricant
sliding Parts and gear wheels.

FMVSS = Federal Motor Vehicle Safety Standard (USA)
UL = Underwriters Laboratories (USA)

General

Material Status

Commercial: Active

Availability

Africa & Middle East

Asia Pacific

Europe

Filler / Reinforcement

Chalk Filler

Features

Alkali Resistant

Copolymer

Fuel Resistant

Good Chemical Resistance

Good Flow

High Hardness

High Rigidity

High Strength

Hydrolysis Resistant

Oxidation Resistant

Solvent Resistant

Uses

Gears

RoHS Compliance

Processing Method

Injection Molding

Resin ID (ISO 1043)

Physical	Nominal Value	Unit	Test Method
Density		g/cm³	ISO 1183
Melt Volume-Flow Rate (MVR) (190°C/2.16 kg)		in³/10min	ISO 1133
Molding Shrinkage			ISO 294-4
Across Flow		%
Flow		%
Water Absorption (Saturation, 73°F)		%	ISO 62
Mechanical	Nominal Value	Unit	Test Method
Tensile Modulus		psi	ISO 527-2/1A/1
Tensile Stress (Yield)		psi	ISO 527-2/1A/50
Tensile Strain (Yield)		%	ISO 527-2/1A/50
Nominal Tensile Strain at Break		%	ISO 527-2/1A/50
Impact	Nominal Value	Unit	Test Method
Charpy Notched Impact Strength			ISO 179/1eA
-22°F		ft·lb/in²
73°F		ft·lb/in²
Thermal	Nominal Value	Unit	Test Method
Heat Deflection Temperature (264 psi, Unannealed)		°F	ISO 75-2/A
Vicat Softening Temperature		°F	ISO 306/B50
Melting Temperature²		°F	ISO 11357-3
CLTE - Flow		in/in/°F	ISO 11359-2
Electrical	Nominal Value	Unit	Test Method
Surface Resistivity		ohms	IEC 60093
Volume Resistivity		ohm·cm	IEC 60093
Relative Permittivity			IEC 60250
100 Hz
1 MHz
Dissipation Factor			IEC 60250
100 Hz
1 MHz
Comparative Tracking Index		V	IEC 60112
Electric Strength		V/mil	IEC 60243-1
Flammability	Nominal Value	Unit	Test Method
Flame Rating - UL			UL 94
0.0591 in
0.118 in
Additional Information	Nominal Value	Unit	Test Method
ISO Type			ISO 9988-1
Related Terminology
Product names can be difficult to match. You may have searched any one of these terms to find this product: Hostaform® C 13031 K, Hostaform C 13031 K, Hostaform® , Hostaform, HostaformC13031K, C 13031 K, C13031, 13031K, C13031K, Acetal Copolymer, Acetal Copolymer, Acetal (POM) Copolymer, Acetal POM Copolymer, Acetal, pom, Ticona, AcetalPOMCopolymer, 13031C
Features
Features may also be described by the following terms: High Hardness, Hard, High Rigidity, High Strength, Good Chemical Resistance, Chemical Resistant, Good Flow.

Injection	Nominal Value	Unit
Processing (Melt) Temp		°F
Mold Temperature		°F
Screw L/D Ratio
Injection Notes
Standard injection moulding machines with three phase (15 to 25 D) plasticating screws will fit.

Notes

¹Typical properties: these are not to be construed as specifications.

²10°C/min

Hostaform® C 13031 K

Acetal (POM) Copolymer

Chalk Filler

Supplied by Ticona