Hostaform C 9021 GV1/20 Ticona Acetal (POM) Copolymer (Glass Fiber Reinforcement, 20%)

Product Description

Chemical abbreviation according to ISO 1043-1: POM
Molding compound ISO 9988- POM-K, M-GNR, 02-003, GF20

POM copolymer

Injection molding type, reinforced with ca. 20 % glass fibers high
resistance to thermal and oxidative degradation reduced thermal
expansion and shrinkage.

UL-registration in natural and black and a thickness more than
1.5 mm as UL 94 HB, temperature index UL 746 B, electrical 105 °C,
mechanical 105 °C

Burning rate ISO 3795 and FMVSS 302 < 100 mm/min for a thickness
more than 1 mm thickness.

Ranges of applications: For molded parts with high strength and
rigidity as well as higher hardness.

FMVSS = Federal Motor Vehicle Safety Standard (USA)
UL = Underwriters Laboratories (USA)

General

Material Status

Commercial: Active

Availability

Africa & Middle East

Asia Pacific

Europe

Latin America

North America

South America

Filler / Reinforcement

Glass Fiber Reinforcement, 20% Filler by Weight

Features

Copolymer

High Hardness

High Heat Resistance

High Rigidity

High Strength

Low Shrinkage

RoHS Compliance

Automotive Specifications

Processing Method

Injection Molding

Multi-Point Data

Isothermal Stress vs. Strain (ISO 11403-1)

Shear Modulus vs. Temperature (ISO 11403-1)

Resin ID (ISO 1043)

Physical	Nominal Value	Unit	Test Method
Density		g/cm³	ISO 1183
Melt Volume-Flow Rate (MVR) (190°C/2.16 kg)		in³/10min	ISO 1133
Water Absorption (Saturation, 73°F)		%	ISO 62
Mechanical	Nominal Value	Unit	Test Method
Tensile Modulus		psi	ISO 527-2/1A/1
Tensile Stress (Break)		psi	ISO 527-2/1A/5
Tensile Strain (Break)		%	ISO 527-2/1A/5
Tensile Creep Modulus			ISO 899-1
1 hr		psi
1000 hr		psi
Flexural Modulus (73°F)		psi	ISO 178
Impact	Nominal Value	Unit	Test Method
Charpy Notched Impact Strength			ISO 179/1eA
-22°F		ft·lb/in²
73°F		ft·lb/in²
Charpy Unnotched Impact Strength			ISO 179/1eU
-22°F		ft·lb/in²
73°F		ft·lb/in²
Thermal	Nominal Value	Unit	Test Method
Heat Deflection Temperature
264 psi, Unannealed		°F	ISO 75-2/A
1160 psi, Unannealed		°F	ISO 75-2/C
Vicat Softening Temperature		°F	ISO 306/B50
Melting Temperature²		°F	ISO 11357-3
CLTE			ISO 11359-2
Flow		in/in/°F
Transverse		in/in/°F
Electrical	Nominal Value	Unit	Test Method
Surface Resistivity		ohms	IEC 60093
Volume Resistivity		ohm·cm	IEC 60093
Relative Permittivity			IEC 60250
100 Hz
1 MHz
Dissipation Factor			IEC 60250
100 Hz
1 MHz
Comparative Tracking Index		V	IEC 60112
Electric Strength		V/mil	IEC 60243-1
Flammability	Nominal Value	Unit	Test Method
Flame Rating - UL			UL 94
0.0591 in
0.118 in
Additional Information	Nominal Value	Unit	Test Method
ISO Type			ISO 9988-1
Related Terminology
Product names can be difficult to match. You may have searched any one of these terms to find this product: Hostaform® C 9021 GV1/20, Hostaform C 9021 GV120, Hostaform® , Hostaform, HostaformC9021GV120, C 9021 GV 1, C 9021 GV1, C 9021 GV 1 20, C9021GV1, C 9021 GV1/20, C 9021 GV120, C 9021 GV1:20, C 9021 GV1+20, C 9021 GV1-20, C 9021 GV1_20, C 9021 GV1 20, C9021, 9021GV, GV1, 120, C9021GV120, Acetal Copolymer, Acetal Copolymer, C9021GV1_20, Acetal (POM) Copolymer, Acetal POM Copolymer, Acetal, pom, Ticona, AcetalPOMCopolymer, 9021C
Features
Features may also be described by the following terms: High Hardness, Hard, High Heat Resistance, High Rigidity, Low Shrinkage, High Strength.
Automotive Specifications
This plastic material has approval for 1 automotive specifications from the following agencies (the number in parentheses shows the number of specifications for that agency): FORD (1).

Injection	Nominal Value	Unit
Processing (Melt) Temp		°F
Mold Temperature		°F
Screw L/D Ratio
Injection Notes
Standard injection moulding machines with three phase (15 to 25 D) plasticating screws will fit.

Notes

¹Typical properties: these are not to be construed as specifications.

²10°C/min

Hostaform® C 9021 GV1/20

Acetal (POM) Copolymer

Glass Fiber Reinforcement, 20%

Supplied by Ticona