Hostaform® C 9021 GV3/30 Ticona Acetal (POM) Copolymer (Glass Bead, 30%)

Product Description

Chemical abbreviation according to ISO 1043-1: POM
Molding compound ISO 9988- POM-K, M-GNR, 02-002, GB30

POM copolymer

Injection molding type, reinforced with ca. 30 % glass spheres high resistance to thermal and oxidative degradation.

UL-registration in natural and a thickness more than 0.81 mm, in black and a thickness more than 1.0 mm as UL94 HB, temperature index UL 746 B for a thickness of 1.57 mm, electrical 105 °C, mechanical 95 °C (tensile impact) and 100 °C (tensile).

Burning rate ISO 3795 and FMVSS 302 < 100 mm/min for a thickness more than 1 mm.

Ranges of applications: For low-warpagee and dimensionally stable molded parts with higher rigidity and hardness.

FMVSS = Federal Motor Vehicle Safety Standard (USA)
UL = Underwriters Laboratories (USA)

General

Material Status

Commercial: Active

Availability

Africa & Middle East

Asia Pacific

Europe

Filler / Reinforcement

Glass Bead, 30% Filler by Weight

Features

Copolymer

Good Dimensional Stability

High Hardness

High Heat Resistance

High Rigidity

Low Warpage

RoHS Compliance

Processing Method

Injection Molding

Multi-Point Data

Isothermal Stress vs. Strain (ISO 11403-1)

Shear Modulus vs. Temperature (ISO 11403-1)

Viscosity vs. Shear Rate (ISO 11403-2)

Resin ID (ISO 1043)

Physical	Nominal Value	Unit	Test Method
Density		g/cm³	ISO 1183
Melt Volume-Flow Rate (MVR) (190°C/2.16 kg)		in³/10min	ISO 1133
Water Absorption (Saturation, 73°F)		%	ISO 62
Mechanical	Nominal Value	Unit	Test Method
Tensile Modulus		psi	ISO 527-2/1A/1
Tensile Stress (Yield)		psi	ISO 527-2/1A/50
Tensile Strain (Yield)		%	ISO 527-2/1A/50
Nominal Tensile Strain at Break		%	ISO 527-2/1A/50
Tensile Creep Modulus			ISO 899-1
1 hr		psi
1000 hr		psi
Flexural Modulus (73°F)		psi	ISO 178
Impact	Nominal Value	Unit	Test Method
Charpy Notched Impact Strength			ISO 179/1eA
-22°F		ft·lb/in²
73°F		ft·lb/in²
Charpy Unnotched Impact Strength			ISO 179/1eU
-22°F		ft·lb/in²
73°F		ft·lb/in²
Thermal	Nominal Value	Unit	Test Method
Heat Deflection Temperature (264 psi, Unannealed)		°F	ISO 75-2/A
Vicat Softening Temperature		°F	ISO 306/B50
Melting Temperature²		°F	ISO 11357-3
CLTE			ISO 11359-2
Flow		in/in/°F
Transverse		in/in/°F
Electrical	Nominal Value	Unit	Test Method
Surface Resistivity		ohm	IEC 60093
Volume Resistivity		ohm·cm	IEC 60093
Relative Permittivity			IEC 60250
100 Hz
1 MHz
Dissipation Factor			IEC 60250
100 Hz
1 MHz
Comparative Tracking Index		V	IEC 60112
Electric Strength		V/mil	IEC 60243-1
Flammability	Nominal Value	Unit	Test Method
Flame Rating - UL			UL 94
0.0319 in
0.0618 in
Fill Analysis	Nominal Value	Unit	Test Method
Melt Density		g/cm³	Internal Method
Melt Specific Heat		Btu/lb/°F	ASTM C351
Melt Thermal Conductivity		Btu·in/hr/ft²/°F	Internal Method
Ejection Temperature		°F
Additional Information	Nominal Value	Unit	Test Method
Effective Thermal Diffusivity		cSt	Internal Method
ISO Type			ISO 9988-1
Related Terminology
Product names can be difficult to match. You may have searched any one of these terms to find this product: Hostaform® C 9021 GV3/30, Hostaform C 9021 GV330, Hostaform® , Hostaform, HostaformC9021GV330, C 9021 GV 3, C 9021 GV3, C 9021 GV 3 30, C9021GV3, C 9021 GV3/30, C 9021 GV330, C 9021 GV3:30, C 9021 GV3+30, C 9021 GV3-30, C 9021 GV3_30, C 9021 GV3 30, C9021, 9021GV, GV3, 330, C9021GV330, Acetal Copolymer, Acetal Copolymer, C9021GV3_30, Acetal (POM) Copolymer, Acetal POM Copolymer, Acetal, pom, Ticona, AcetalPOMCopolymer, 9021C
Features
Features may also be described by the following terms: High Hardness, Hard, High Heat Resistance, High Rigidity, Low Warpage, Low Warp, Good Dimensional Stability, Dimensionally Stable.

Injection	Nominal Value	Unit
Processing (Melt) Temp		°F
Mold Temperature		°F
Screw L/D Ratio
Injection Notes
Standard injection moulding machines with three phase (15 to 25 D) plasticating screws will fit.

Notes

¹Typical properties: these are not to be construed as specifications.

²10°C/min

Hostaform® C 9021 GV3/30

Acetal (POM) Copolymer

Glass Bead, 30%

Supplied by Ticona