| Density |
|
g/cm³
|
ASTM D1505 |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) |
|
g/10 min
|
ASTM D1238 |
| Film Thickness - Tested |
|
mil
|
|
| Secant Modulus |
|
|
ASTM D882 |
|
1% Secant, MD: 1.5 mil, Blown Film
|
|
psi
|
|
|
1% Secant, TD: 1.5 mil, Blown Film
|
|
psi
|
|
| Tensile Strength |
|
|
ASTM D882 |
|
MD: Yield, 1.5 mil, Blown Film
|
|
psi
|
|
|
TD: Yield, 1.5 mil, Blown Film
|
|
psi
|
|
|
MD: Break, 1.5 mil, Blown Film
|
|
psi
|
|
|
TD: Break, 1.5 mil, Blown Film
|
|
psi
|
|
| Tensile Elongation |
|
|
ASTM D882 |
|
MD: Break, 1.5 mil, Blown Film
|
|
%
|
|
|
TD: Break, 1.5 mil, Blown Film
|
|
%
|
|
| Dart Drop Impact (1.5 mil, Blown Film) |
|
g
|
ASTM D1709 |
| Elmendorf Tear Strength |
|
|
ASTM D1922 |
|
MD: 1.5 mil, Blown Film
|
|
g
|
|
|
TD: 1.5 mil, Blown Film
|
|
g
|
|
| Brittleness Temperature |
|
°F
|
ASTM D746 |
| Vicat Softening Temperature |
|
°F
|
ASTM D1525 |
| Melting Temperature |
|
°F
|
|
| Gloss (45°, 1.50 mil, Blown Film) |
|
|
ASTM D2457 |
| Clarity |
|
|
ASTM D1746 |
| Haze (1.50 mil, Blown Film) |
|
%
|
ASTM D1003 |
|
Blow Up Ratio: 2
|
|
Product names can be difficult to match. You may have searched any one of these terms to find this product: TAISOX 3220, TAISOX , TAISOX3220, 3220, Polyethylene, Linear Low Density, Polyethylene Linear Low Density, LLDPE, Polyethylene, PE, Formosa Chemicals, PolyethyleneLinearLowDensity
|
|
Features may also be described by the following terms: Low Density, Low Specific Gravity, Good Drawdown, Good draw down, Good Heat Seal.
|
|
Uses may also be described by the following terms: Stretch Wrap.
|