Density
|
|
g/cm³
|
ASTM D1505 |
|
Melt Mass-Flow Rate (MFR) (190°C/2.16 kg)
|
|
g/10 min
|
ASTM D1238 |
|
Film Thickness - Tested
|
|
mil
|
|
|
Secant Modulus
|
|
|
ASTM D882 |
|
1% Secant, MD: 1.5 mil, Blown Film
|
|
psi
|
|
|
1% Secant, TD: 1.5 mil, Blown Film
|
|
psi
|
|
|
Tensile Strength
|
|
|
ASTM D882 |
|
MD: Yield, 1.5 mil, Blown Film
|
|
psi
|
|
|
TD: Yield, 1.5 mil, Blown Film
|
|
psi
|
|
|
MD: Break, 1.5 mil, Blown Film
|
|
psi
|
|
|
TD: Break, 1.5 mil, Blown Film
|
|
psi
|
|
|
Tensile Elongation
|
|
|
ASTM D882 |
|
MD: Break, 1.5 mil, Blown Film
|
|
%
|
|
|
TD: Break, 1.5 mil, Blown Film
|
|
%
|
|
|
Dart Drop Impact (1.5 mil, Blown Film)
|
|
g
|
ASTM D1709 |
|
Elmendorf Tear Strength
|
|
|
ASTM D1922 |
|
MD: 1.5 mil, Blown Film
|
|
g
|
|
|
TD: 1.5 mil, Blown Film
|
|
g
|
|
|
Brittleness Temperature
|
|
°F
|
ASTM D746 |
|
Vicat Softening Temperature
|
|
°F
|
ASTM D1525 |
|
Melting Temperature
|
|
°F
|
|
|
Gloss (45°, 1.50 mil, Blown Film)
|
|
|
ASTM D2457 |
|
Clarity
|
|
|
ASTM D1746 |
|
Haze (1.50 mil, Blown Film)
|
|
%
|
ASTM D1003 |
|
Blow Up Ratio: 2
|
|
Product names can be difficult to match. You may have searched any one of these terms to find this product: TAISOX 2210, TAISOX , TAISOX2210, 2210, Polyethylene, Linear Low Density, Polyethylene Linear Low Density, LLDPE, Polyethylene, PE, Formosa Chemicals, PolyethyleneLinearLowDensity
|
|
Features may also be described by the following terms: Low Density, Low Specific Gravity, Good Heat Seal, High Impact Resistance, Good Tear Strength, Good Puncture Resistance, Puncture Resistant, Medium Antiblocking, Medium Antiblock.
|
|
Uses may also be described by the following terms: Heavy-duty Bags, Heavy Duty Bags, Stretch Wrap.
|