Specific Gravity
|
|
|
|
|
--
|
|
|
ASTM D792 |
|
--
|
|
g/cm³
|
ISO 1183 |
|
Melt Mass-Flow Rate (MFR) (230°C/2.16 kg)
|
|
g/10 min
|
ASTM D1238, ISO 1133 |
|
Molding Shrinkage
|
|
|
ASTM D955 |
|
Flow
|
|
in/in
|
|
|
Across Flow
|
|
in/in
|
|
|
Water Absorption (73°F, 24 hr)
|
|
%
|
ASTM D570, ISO 62 |
|
Tensile Strength (Yield)
|
|
psi
|
ASTM D638, ISO 527-2 |
|
Tensile Elongation (Break)
|
|
%
|
ASTM D638, ISO 527-2 |
|
Flexural Modulus
|
|
psi
|
ASTM D790, ISO 178 |
|
Notched Izod Impact
|
|
|
ASTM D256 |
|
-4°F
|
|
ft·lb/in
|
|
|
32°F
|
|
ft·lb/in
|
|
|
73°F
|
|
ft·lb/in
|
|
|
Deflection Temperature Under Load
|
|
|
|
|
66 psi, Unannealed
|
|
°F
|
ASTM D648, ISO 75-2/B |
|
264 psi, Unannealed
|
|
°F
|
ASTM D648, ISO 75-2/A |
|
Vicat Softening Temperature
|
|
|
|
|
--
|
|
°F
|
ASTM D1525 2, ISO 306/A50 2 |
|
--
|
|
°F
|
ASTM D1525 3, ISO 306/B50 3 |
|
CLTE - Flow
|
|
in/in/°F
|
ASTM D696 |
|
Comparative Tracking Index (Solution A)
|
|
V
|
IEC 60112 |
|
Flame Rating - UL (0.0630 in)
|
|
|
UL 94 |
|
Notched Izod Impact Strength , ISO 180, 23°C: 50 J/m
Notched Izod Impact Strength , ISO 180, -20°C: 25 J/m
Notched Izod Impact Strength , ISO 180, 0°C: 35 J/m
Melt Mass-Flow Rate , ISO 1133, 230/2.16 kg: 4 to 10 g/10min
Melt Mass-Flow Rate , ASTM D1238, 230/2.16 kg: 4 to 10 g/10min
CTI IEC 112, IEC 60112, Method A: >600 V
|
|
Product names can be difficult to match. You may have searched any one of these terms to find this product: HAIPLEN EP50 C10 Z1, HAIPLEN , HAIPLENEP50C10Z1, EP 50 C 10 Z 1, EP50 C10 Z1, EP50, 50C, C10, 10Z, Z1, EP50C10Z1, Polypropylene Copolymer, PP Copolymer, Polypropylene, PP, Taro Plast, PolypropyleneCopolymer, PPCopolymer, 50EP
|
|
Features may also be described by the following terms: Good Surface Finish, Heat Stabilized, Heat-ageing Stabilized, Heat Ageing Stabilized, Heat-aging Stabilized, Heat Aging Stabilized, Detergent Resistant, Detergent Resistance.
|